PA66 Leona™ 1402SH XA1 ASAHI JAPAN
194
Unit Price:$3085 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 209MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity Excellent articulation Plasticity and demolding Used for rapid modeling c
- Application Areas:Washer Hose Wire sheath Application in the automo Laptop case parts Wire and cable applicatio Joint Clip
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.3to2.0 | % |
| Water absorption rate | Saturation,23°C | -- | % | |
| Equilibrium,23°C,50%RH | ISO62 | -- | % | |
| Moisture absorption rate | 湿 | 2.5 | % | |
| Shrinkage rate | 干 | 旭化成方法 | 1.3-2.0 | % |
| Wear rate | 湿 | ASTM D-1044 | 7 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 干(湿) | ASTM D-638 | 79(55) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 50(270) | % |
| Rockwell hardness | 干(湿) | ASTM D-785 | 80(55) | M Scale |
| Flexural strength | 干(湿) | ASTM D-790 | 118(50) | Mpa |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 39(196) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 120(108) | R scale |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 2.8(1.0) | GPa |
| Tensile modulus | 23°C | ISO527-2 | 3000 | Mpa |
| tensile strength | ASTMD638 | 79.0 | Mpa | |
| Yield,23°C | ISO527-2 | 82.0 | Mpa | |
| elongation | Yield,23°C | ISO527-2 | 4.5 | % |
| Break | ASTMD638 | 50 | % | |
| Break,23°C | ISO527-2 | -- | % | |
| Bending modulus | ASTMD790 | 2800 | Mpa | |
| 23°C | ISO178 | 2600 | Mpa | |
| bending strength | ASTMD790 | 118 | Mpa | |
| 23°C | ISO178 | 111 | Mpa | |
| Taber abraser | 1000Cycles | ASTMD1044 | -- | mg |
| Impact strength of simply supported beam without notch | ISO179 | NoBreak | ||
| Rockwell hardness | M-Sale | ASTMD785 | 80 | |
| R-Sale | ASTMD785 | 120 | ||
| M-Sale | ISO2039-2 | 80 | ||
| R-Sale | ISO2039-2 | 120 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 230 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 162 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 70.0 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 62.0 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 8E-05 | cm/cm/°C |
| specific heat | 1670 | J/kg/°C | ||
| thermal conductivity | 0.20 | W/m/K | ||
| Flame retardant grade | 干 | UL 94 | V-2 | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 70 | °C |
| 0.46MPa,干 | ASTM D-648 | 230 | °C | |
| Specific heat capacity | 干 | 1670 | J/(kg.k) | |
| Thermal conductivity | 干 | 0.2 | W/(m.K) | |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 8 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+13 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+14 | ohms·cm |
| Dielectric strength | IEC60243-1 | 20 | KV/mm | |
| Leakage Trace Index | 3.00mm | IEC60112 | 525 | V |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen index | 干 | ASTM D-2863 | 26 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-2 | |
| Extreme Oxygen Index | ASTMD2863 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.