PA66 Durethan® D.AKV30H2.0 LANXESS GERMANY
250
Unit Price:$4473 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: LANXESS Germany
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.70 | g/cm³ | |
| Shrinkage rate | TD:290°C,2.00mm2 | ISO294-4 | 0.93 | % |
| TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.13 | % | |
| MD:290°C,2.00mm2 | ISO294-4 | 0.39 | % | |
| MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 5.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ASTMD638 | 9170 | Mpa |
| 23°C | ISO527-2/1 | 10000 | Mpa | |
| tensile strength | Break,23°C | ASTMD638 | 170 | Mpa |
| Break,23°C | ISO527-2/5 | 175 | Mpa | |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Break,23°C | ISO527-2/5 | 3.0 | % | |
| Nominal tensile fracture strain | 23°C | ISO527-2/50 | 4.4 | % |
| Bending modulus | 23°C | ASTMD790 | 8690 | Mpa |
| 23°C | ISO178/A | 9200 | Mpa | |
| bending strength | 23°C | ASTMD790 | 270 | Mpa |
| 3.5%Strain | ISO178/A | 265 | Mpa | |
| 23°C | ISO178 | 270 | Mpa | |
| FlexuralStrainatFlexuralStrength6(23°C) | 4.0 | % | ||
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 60 | kJ/m² |
| 23°C | ISO179/1eU | 75 | kJ/m² | |
| Cantilever beam without notch impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
| 23°C | ISO180/1U | 60 | kJ/m² | |
| Ball pressure hardness | ISO2039-1 | 220 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| RTIElec | 0.75mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| RTI Imp | 0.75mm | UL746 | 90.0 | °C |
| 1.5mm | UL746 | 105 | °C | |
| RTIStr | 0.75mm | UL746 | 110 | °C |
| 1.5mm | UL746 | 115 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 250 | °C | |
| 1.8MPa,Unannealed,4.00mm | ASTMD648 | >249 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | >240 | °C | |
| vicat softening point | -- | ISO306/B50 | 230 | °C |
| -- | ISO306/B120 | >230 | °C | |
| Ball Pressure Test | 253°C | IEC60695-10-2 | Pass | |
| Melting temperature | ISO11357-3 | 263 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+15 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 35 | KV/mm |
| 23°C,3.00mm | IEC60243-1 | 30 | KV/mm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Dissipation factor | 23°C,50Hz | IEC60250 | 0.012 | |
| 23°C,100Hz | IEC60250 | 0.012 | ||
| 23°C,1MHz | IEC60250 | 0.0190.019 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 475 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | --7 | ISO6603-2 | 2.80 | J |
| --8 | ISO6603-2 | 2.30 | J | |
| Membrane piercing force | --7 | ISO6603-2 | 900 | N |
| --8 | ISO6603-2 | 800 | N |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 1.6mm | UL94 | HB | ||
| 3.0mm | UL94 | HB | ||
| 3.2mm | UL94 | HB | ||
| Burning wire flammability index | 0.8mm | IEC60695-2-12 | 700 | °C |
| 1.6mm | IEC60695-2-12 | 700 | °C | |
| 3.0mm | IEC60695-2-12 | 700 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 23 | % | |
| BurningBehavior | >1.00mm | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA66,GHR,14-100,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.