PA66 Amilan® CM3001G15 TORAY PLASTICS CHENGDU
150
Unit Price:$4018 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Electrical components Electrical appliances Automotive sector Electronic field
- Color:--
- Grade:Enhance wear resistance level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | 23°C | ISO 1183 | 1.37 | g/cm³ |
| Shrinkage rate | Across Flow : 3.00 mm | 内部方法 | 0.60 到 0.90 | % |
| 流量 : 3.00 mm | 内部方法 | 0.20 到 0.50 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.60 | % |
| Saturation, 23°C | ISO 62 | 5.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale, 23°C | ISO 2039-2 | 97 | |
| R -Sale, 80°C | ISO 2039-2 | 24 | ||
| R -Sale, 23°C | ISO 2039-2 | 121 | ||
| tensile strength | -40°C | ISO 527-2 | 235 | Mpa |
| 23°C | ISO 527-2 | 190 | Mpa | |
| 80°C | ISO 527-2 | 120 | Mpa | |
| elongation | Break, -40°C | ISO 527-2 | 2.0 | % |
| Break, 23°C | ISO 527-2 | 2.5 | % | |
| Break, 80°C | ISO 527-2 | 5.0 | % | |
| Bending modulus | -40°C | ISO 178 | 11600 | Mpa |
| 23°C | ISO 178 | 9500 | Mpa | |
| 80°C | ISO 178 | 5800 | Mpa | |
| bending strength | -40°C | ISO 178 | 325 | Mpa |
| 23°C | ISO 178 | 290 | Mpa | |
| 80°C | ISO 178 | 190 | Mpa | |
| Compressive stress | -40°C | ISO 604 | 250 | Mpa |
| 23°C | ISO 604 | 180 | Mpa | |
| 80°C | ISO 604 | 110 | Mpa | |
| shear strength | 23°C | ASTM D732 | 95.0 | Mpa |
| Taber abraser | 1000 Cycles | ISO 9352 | 0.400 | mg |
| Friction coefficient - vs. Metal | Suzuki Method | 0.15 | ||
| Charpy Notched Impact Strength | -40°C | ISO 179 | 10 | kJ/m² |
| 23°C | ISO 179 | 13 | kJ/m² | |
| Impact strength of simply supported beam without notch | -40°C | ISO 179 | 60 | kJ/m² |
| 23°C | ISO 179 | 65 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 | °C |
| Melting temperature | DSC | 265 | °C | |
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 2.0E-5 到 3.0E-5 | cm/cm/°C | |
| specific heat | 1800 | J/kg/°C | ||
| thermal conductivity | 0.40 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | 1.0E+13 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 20 | KV/mm | |
| Dielectric constant | 23°C, 50 Hz | IEC 60250 | 4.60 | |
| 23°C, 1 kHz | IEC 60250 | 4.40 | ||
| 23°C, 1 MHz | IEC 60250 | 3.90 | ||
| Dissipation factor | 23°C, 50 Hz | IEC 60250 | 0.020 | |
| 23°C, 1 kHz | IEC 60250 | 0.020 | ||
| 23°C, 1 MHz | IEC 60250 | 0.020 | ||
| Arc resistance | UL 746 | 114 | sec |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.79 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.