PA66 CELSTRAN® GF50-01 CELANESE USA
140
Unit Price:$4355 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 80MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced Filler: Long glass fiber 50% filler by weight
- Application Areas:Electrical components Electronic and electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | MD | ASTMD955 | 0.050to0.10 | % |
| TD | ASTMD955 | 0.20to0.30 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -40°C | ASTMD638 | 16000 | Mpa |
| 23°C | ASTMD638 | 17600 | Mpa | |
| 121°C | ASTMD638 | 9030 | Mpa | |
| ISO527-2/1A/1 | 16000 | Mpa | ||
| 拉伸强度 | 断裂,-40°C | ASTMD638 | 322 | Mpa |
| 断裂,23°C | ASTMD638 | 272 | Mpa | |
| Break,121°C | ASTMD638 | 123 | Mpa | |
| 断裂 | ISO527-2/1A/5 | 245 | Mpa | |
| 伸长率 | 断裂,-40°C | ASTMD638 | 2.6 | % |
| 断裂,23°C | ASTMD638 | 2.2 | % | |
| Break,121°C | ASTMD638 | 2.3 | % | |
| 断裂 | ISO527-2/1A/5 | 2.0 | % | |
| 弯曲模量 | 23°C | ISO178 | 14700 | Mpa |
| 弯曲强度 | 23°C | ISO178 | 390 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 1.8MPa,未退火 | ASTMD648 | 213 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 215 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.