Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced Filler: Glass fiber reinf Glass fiber content is 30 Flame retardant grade UL9
- Application Areas:Hose Joint switch Electronic field Electrical field Electrical components Electrical/Electronic App switch Laptop case Joint switch Other electrical and elec
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Wear rate | 湿 | ASTM D-1044 | 29 | |
| Shrinkage rate | TD | 内部方法 | 0.70 | % |
| MD | 内部方法 | 0.30 | % | |
| 吸水率(Saturation,23°C) | 内部方法 | -- | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | -- | % |
| Moisture absorption rate | 湿 | 0.6 | % | |
| Shrinkage rate | 干 | 旭化成方法 | 0.3-0.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 11700 | Mpa |
| tensile strength | ASTMD638 | 167 | Mpa | |
| Break,23°C | ISO527-2 | 174 | Mpa | |
| elongation | Break | ASTMD638 | 2.5 | % |
| Break,23°C | ISO527-2 | 2.0 | % | |
| Bending modulus | ASTMD790 | 10800 | Mpa | |
| 23°C | ISO178 | 10300 | Mpa | |
| bending strength | ASTMD790 | 250 | Mpa | |
| 23°C | ISO178 | 259 | Mpa | |
| Taber abraser | 1000Cycles | ASTMD1044 | -- | mg |
| Impact strength of simply supported beam without notch | ISO179 | 50 | kJ/m² | |
| Rockwell hardness | M-Scale | ASTMD785 | 100 | |
| Flexural strength | 干(湿) | ASTM D-790 | 250(221) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 2.5(2.7) | % |
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 88(98) | J/m |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 10.8(8.3) | GPa |
| tensile strength | 干(湿) | ASTM D-638 | 167(142) | Mpa |
| Rockwell hardness | 干(湿) | ASTM D-785 | 100(60) | M Scale |
| M-Scale | ISO2039-2 | 100 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 260 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 262 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 252 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 245 | °C | |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 3E-05 | cm/cm/°C |
| Flame retardant grade | 干 | UL 94 | V-0 | |
| Linear coefficient of thermal expansion | 干 | ASTM D-696 | 3 | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 252 | °C |
| 0.46MPa,干 | ASTM D-648 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | ASTMD149 | 28 | KV/mm | |
| IEC60243-1 | 28 | KV/mm | ||
| Leakage Trace Index | 3.00mm | IEC60112 | 275 | V |
| Surface resistivity | ASTMD257 | 1E+14 | ohms | |
| IEC60093 | 1E+14 | ohms | ||
| Volume resistivity | ASTMD257 | 1E+15 | ohms·cm | |
| 23°C | IEC60093 | 1E+15 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 | |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.