Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance
- Application Areas:Fitness equipment｜Bottle cap｜Automotive sector
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ISO 1183 | 1.07 g/cm³ | |
| Modeling Shrinkage | 横向流量 | ISO 294-4 | 1.4 % |
| 流量 | ISO 294-4 | 1.8 % | |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 1.1 % |
| 饱和, 23°C, 2.00 mm | ISO 62 | 6.5 % | |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 % | |
| Viscosity number | ISO 307 | 130 cm³/g |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 157 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 63.0 °C | |
| Glass Transition Temperature | ISO 11357-2 | 75.0 °C | |
| Vicat Softening Temperature | ISO 306/B50 | 205 °C | |
| Melting Temperature | ISO 11357-3 | 262 °C | |
| Linear thermal expansion coefficient | 流动 : 23 到 55°C | ASTM E831 | 1.4E-4 cm/cm/°C |
| 流动 | ISO 11359-2 | 1.4E-4 cm/cm/°C | |
| 流动 : -40 到 23°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| 流动 : 55 到 160°C | ISO 11359-2 | 1.6E-4 cm/cm/°C | |
| 横向 : 23 到 55°C | ASTM E831 | 1.3E-4 cm/cm/°C | |
| 横向 | ISO 11359-2 | 1.3E-4 cm/cm/°C | |
| 横向 : -40 到 23°C | ISO 11359-2 | 1.1E-4 cm/cm/°C | |
| 横向 : 55 到 160°C | ISO 11359-2 | 1.3E-4 cm/cm/°C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning Rate | 1.00 mm | ISO 3795 | < 100 mm/min |
| UL flame retardant rating | 0.8 mm | UL 94, IEC 60695-11-10, -20 | HB |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| Oxygen Index | ISO 4589-2 | 20 % | |
| FMVSS Flammability | FMVSS 302 | B |
| Fill Analysis | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Ejection Temperature | 190 °C |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | ISO 527-2 | 2000 Mpa | |
| Tensile Stress | 50% 应变 | ISO 527-2 | 49.0 Mpa |
| Tensile Strain | 断裂 | ISO 527-2 | > 50 % |
| Tensile Creep Modulus | 1 hr | ISO 899-1 | -- Mpa |
| 1000 hr | ISO 899-1 | -- Mpa | |
| Flexural Modulus | ISO 178 | 1800 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 62631-3-2 | -- ohms | |
| Volume Resistivity | IEC 62631-3-1 | > 1.0E+13 ohms·m | |
| Dielectric Strength | IEC 60243-1 | 25 KV/mm | |
| Relative Permittivity | 1 MHz | IEC 62631-2-1 | 3.30 |
| 100 Hz | IEC 62631-2-1 | 3.50 | |
| Dissipation Factor? | 100 Hz | IEC 62631-2-1 | 5.0E-3 |
| 1 MHz | IEC 62631-2-1 | 0.010 | |
| Comparative Tracking Index | IEC 60112 | 600 V |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 80 °C | ||
| Drying time - Hot air dryer | 2.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.20 % | ||
| Processing (Melt) Temp | 280 到 300 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Mold Temperature | 50 到 100 °C | ||
| Mold Temperature, Optimum | 80 °C | ||
| Holding Pressure | 50.0 到 100 Mpa | ||
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 s/mm | ||
| Maximum Screw Tangential Speed | 18 m/min |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 kJ/m² |
| 23°C, 局部断裂 | ISO 179/1eA | 70 kJ/m² | |
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | -- |
| Notched Izod Impact Strength | -40°C | ISO 180/1A | 20 kJ/m² |
| -30°C | ISO 180/1A | 15 kJ/m² | |
| 23°C | ISO 180/1A | 80 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.