PA66 Zytel® 408HS DUPONT USA
158
Unit Price:$5588 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Material Certification
Technical Data Sheet
Material Description
- Material Properties:enhance｜Toughening｜Thermal stability｜High impact resistance｜High temperature resistan
- Application Areas:Industrial machinery｜Automotive sector
- Color:--
- Grade:Special level
Material Certification
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Moisture Absorption | 24小时浸渍(23℃) | ASTM D-570 | DAM｜1.2 % |
| 24小时浸渍(23℃) | ASTM D-570 | 50%RH｜- % | |
| 饱和(23℃) | ASTM D-570 | DAM｜7.0 % | |
| 饱和(23℃) | ASTM D-570 | 50%RH｜- % | |
| Moisture Absorption (24hr) | ASTM D570 | 1.2 % | |
| Moisture Absorption (Saturation) | ASTM D570 | 7.0 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melting Temperature | 255 ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 7×10-5 mm/mm.℃ | |
| Thermal distortion temperature | (0.5)×106Pa | ASTM D-648 | DAM｜230 °C |
| (0.5)×106Pa | ASTM D-648 | 50%RH｜- °C | |
| Flame Rating | UL 94 | DAM｜94 | |
| UL 94 | 50%RH｜HB | ||
| Peak Crystallization Temperature? | ASTM D-2177 | DAM｜270 °C | |
| ASTM D-2177 | 50%RH｜- °C | ||
| Coefficient of Linear Thermal Expansion | ASTM D-696 | DAM｜7×10-5 m/m/℃ | |
| ASTM D-696 | 50%RH｜- m/m/℃ | ||
| Heat Deflection Temperature | 13.8MPa，50℃ | ASTM D-621 | DAM｜1.4 % |
| 13.8MPa，50℃ | ASTM D-621 | 50%RH｜- % | |
| Melting Temperature | Fisher Johns法 | ASTM D-789 | 255 °C |
| Fisher Johns法 | ASTM D-789 | 255 °C | |
| Thermal distortion temperature | 18×106Pa | ASTM D-648 | DAM｜75 °C |
| 18×106Pa | ASTM D-648 | 50%RH｜- °C | |
| Brittleness Temperature | ASTM D-746 | DAM｜-104 °C | |
| ASTM D-746 | 50%RH｜-84 °C | ||
| Heat Deflection Temperature | 66 psi， 未退火 | ASTM D648 | 184 °C |
| Coefficient of Linear Thermal Expansion | 平行流动方向 | ASTM E831 | 0.00010 cm/cm/ ℃ |
| Flame retardant grade | UL 94 | HB | |
| Oxygen Index | ASTM D2863 | 23 % |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dielectric Constant | ASTM D150/IEC 60250 | 3.1 | |
| Volume Resistivity | ASTM D257/IEC 60093 | 10 Ω.cm | |
| ASTM D-257 | DAM｜1013 Ω.m | ||
| ASTM D-257 | 50%RH｜1013 Ω.m | ||
| Dielectric Constant | 103Hz(cps) | ASTM D-150 | DAM｜3.1 |
| 100Hz(cps) | ASTM D-150 | 50%RH｜4.8 | |
| Dissipation Factor? | 100Hz(cps) | ASTM D-150 | DAM｜0.02 |
| 100Hz(cps) | ASTM D-150 | 50%RH｜0.1 | |
| 103Hz(cps) | ASTM D-150 | DAM｜0.02 | |
| 103Hz(cps) | ASTM D-150 | 50%RH｜0.11 | |
| 106Hz(cps) | ASTM D-150 | DAM｜0.02 | |
| 106Hz(cps) | ASTM D-150 | 50%RH｜0.10 | |
| Dielectric Constant | 106Hz(cps) | ASTM D-150 | DAM｜2.9 |
| 106Hz(cps) | ASTM D-150 | 50%RH｜3.3 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Elongation?(Break) | ASTM D638/ISO 527 | 80 % | |
| Tensile Strength | ASTM D638/ISO 527 | 62.1 kg/cm²(MPa)[Lb/in²] | |
| Tensile Elongation | ASTM D638/ISO 527 | 60.7 % | |
| Rockwell hardness R | ASTM D-785 | 50%RH｜R102 | |
| Tensile Elongation (Break) | ASTM D-638 | DAM｜5 % | |
| ASTM D-638 | 50%RH｜15 % | ||
| Tensile Strength (Yield) | 23℃ | DAM｜60.7 Mpa | |
| 23℃ | 50%RH｜51.7 Mpa | ||
| Tensile Impact Strength | 长试样23℃ | ASTM D-1822 | DAM｜550 kJ/m² |
| 长试样23℃ | ASTM D-1822 | 50%RH｜1680 kJ/m² | |
| 短试样23℃ | ASTM D-1822 | DAM｜189 kJ/m² | |
| 短试样23℃ | ASTM D-1822 | 50%RH｜265 kJ/m² | |
| Tensile Strength | 23℃ | ASTM D-638 | DAM｜62.1 Mpa |
| Tensile Elongation?(Break) | 23℃ | ASTM D-638 | DAM｜80 % |
| 23℃ | ASTM D-638 | 50%RH｜270 % | |
| Tensile Modulus | 23℃ | ASTM D-790 | DAM｜1965 Mpa |
| 23℃ | ASTM D-790 | 50%RH｜1103 Mpa | |
| Rockwell Hardness(M-Scale) | ASTM D-785 | DAM｜M71 | |
| ASTM D-785 | 50%RH｜M50 | ||
| Notched Izod Impact Strength | 23℃ | ASTM D-256 | DAM｜230 J/m |
| 23℃ | ASTM D-256 | 50%RH｜240 J/m | |
| Durometer Hardness | ASTM D-676 | DAM｜83 | |
| ASTM D-676 | 50%RH｜76 | ||
| Rockwell hardness R | ASTM D-785 | DAM｜R115 | |
| Tensile Strength | 23℃ | ASTM D-638 | 50%RH｜51.7 Mpa |
| Tensile Strength (Yield) | ASTM D638 | 62.7 Mpa | |
| Flexural Modulus | ASTM D790 | 2070 Mpa | |
| Tensile Elongation?(Break) | ASTM D638 | 50 % | |
| Notched Impact Strength | ASTM D256 | 134 J/m |
| Other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 注塑级,良好的热稳定性 | ||
| Oxygen Transmission Rate | ASTM D-2863 | DAM｜19 % | |
| ASTM D-2863 | 50%RH｜20 % |
| Physical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.09 | |
| Moisture Absorption 23℃/24H | ASTM D570/ISO 62 | 1.2 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.