PA66 Amilan® CM3001R TORAY JAPAN
129
Unit Price:$3793 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 61.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage
- Application Areas:OA device
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.19 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.1 | % | |
| Filling content | 40 | wt% | ||
| Water absorption rate | -，23℃,24hrs | D570 | 0.6 | % |
| -，23℃,水中 | D570 | 5.1 | % | |
| Shrinkage rate | MD:3.00mm3 | % | 0.70到1.0 | -- |
| Water absorption rate | 23°C,24hr | % | 0.60 | -- |
| Saturation,23°C | % | 5.1 | -- | |
| Shrinkage rate | TD:3.00mm2 | % | 1.0到1.4 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale,23°C | 83 | -- | |
| R-Sale,23°C | 120 | -- | ||
| tensile strength | -40°C | MPa | 120 | -- |
| 23°C | MPa | 95.0 | 70.0 | |
| 80°C | MPa | 40.0 | -- | |
| elongation | Break,-40°C | % | 3.0 | -- |
| Break,23°C | % | 3.5 | 5.0 | |
| Tensile yield strength | -，-40℃ | D638 | 120 | Mpa |
| -，23℃ | D638 | 95 | Mpa | |
| -，80℃ | D638 | 40 | Mpa | |
| elongation at break | -，-40℃ | D638 | 5.0 | % |
| -，23℃ | D638 | 6.0 | % | |
| -，80℃ | D638 | 8.5 | % | |
| elongation | Break,80°C | % | 5.0 | -- |
| Bending modulus | -40°C | MPa | 6200 | -- |
| 23°C | MPa | 5800 | 3000 | |
| 80°C | MPa | 2000 | -- | |
| bending strength | -40°C | MPa | 185 | -- |
| 23°C | MPa | 155 | ||
| 80°C | MPa | 65.0 | -- | |
| -，-40℃ | D790 | 180 | Mpa | |
| -，23℃ | D790 | 150 | Mpa | |
| -，80℃ | D790 | 60 | Mpa | |
| Bending modulus | -，-40℃ | D790 | 6.4 | GPa |
| -，23℃ | D790 | 6.0 | GPa | |
| -，80℃ | D790 | 2.1 | GPa | |
| impact strength | 23℃ | D256 | 45 | J/m |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 45 | kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 12 | % | |
| tensile strength | ASTM D638/ISO 527 | 85 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 120 | ||
| Bending modulus | ASTM D790/ISO 178 | 3500 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 125 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 224 | ℃（℉） | |
| melting point | 265 | ℃（℉） | ||
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 243 | -- |
| 1.8MPa,Unannealed | °C | 185 | -- | |
| Melting temperature | °C | 265 | -- | |
| melting point | DSC | 265 | °C | |
| Hot deformation temperature | -，0.46Mpa | D648 | 243 | °C |
| -，1.86MPa | D648 | 185 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 | Ω.cm |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 3mmt | 1.0-1.4 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.