Material Description
Technical Data Sheet
Material Description
- Material Properties:dimensional stability Conductive
- Application Areas:Electrical components Electrical field Electronic field Switch panel Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate - flow rate | 内部方法 | 0.50 到 1.3 | % | |
| Water absorption rate | Saturation, 23°C | -- | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | -- | % | |
| density | ASTM D792/ISO 1183 | 1.48 | ||
| Shrinkage rate | ASTM D955 | 0.5-1.3 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.5 | % | |
| Moisture absorption rate | 湿 | 1.5 | % | |
| Shrinkage rate | 干 | 旭化成方法 | 0.5-1.3 | % |
| Wear rate | 湿 | ASTM D-1044 | 8 | ×10-6kg/1000times |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam notch impact strength | 干(湿) | ASTM D-256 | 34(39) | J/m |
| Rockwell hardness | 干(湿) | ASTM D-785 | 85(-) | M Scale |
| Scratch resistance coefficient | 干(湿) | ASTM D-790 | 5.9(2.9) | GPa |
| tensile strength | 干(湿) | ASTM D-638 | 88(64) | Mpa |
| Flexural strength | 干(湿) | ASTM D-790 | 147(93) | Mpa |
| Fracture elongation rate | 干(湿) | ASTM D-638 | 3(3.5) | % |
| Rockwell hardness | ASTM D785 | M85 | ||
| Bending modulus | ASTM D790/ISO 178 | 5880(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 147(MPa) | kg·cm/cm(J/M)ft·lb/in | |
| Rockwell hardness | M-Scale | ASTM D785 | 85 | |
| M -Sale | ISO 2039-2 | 85 | ||
| Tensile modulus | 23°C | ISO 527-2 | 7000 | Mpa |
| tensile strength | Break, 23°C | ISO 527-2 | 85.0 | Mpa |
| -- | ASTM D638 | 88.0 | Mpa | |
| elongation | Break | ASTM D638 | 3.0 | % |
| Break, 23°C | ISO 527-2 | 2.0 | % | |
| Bending modulus | -- | ASTM D790 | 5900 | Mpa |
| 23°C | ISO 178 | 7400 | Mpa | |
| bending strength | -- | ASTM D790 | 147 | Mpa |
| 23°C | ISO 178 | 140 | Mpa | |
| Taber abraser | 1000 Cycles | ASTM D1044 | -- | mg |
| Impact strength of simply supported beam without notch | ISO 179 | 51 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ASTM D648 | 250 | °C |
| 0.45 MPa, Unannealed | ISO 75-2/B | 249 | °C | |
| 1.8 MPa, Unannealed | ASTM D648 | 191 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 188 | °C | |
| Linear coefficient of thermal expansion - flow | ASTM D696 | 4.0E-5 | cm/cm/°C | |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 191 | ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 4 | mm/mm.℃ | |
| 干 | ASTM D-696 | 4 | ×10-5/K | |
| Hot deformation temperature | 1.82MPa,干 | ASTM D-648 | 191(250) | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTM D495/IEC 60112 | 150 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.