PA66 Vydyne® M344 ASCEND USA
116
Unit Price:$4093 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Toughening Lubricity Flame retardant
- Application Areas:Industrial applications Electronic field Electrical field
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:23°C,2.00mm | ISO294-4 | 1.8 | % |
| MD:23°C,2.00mm | ISO294-4 | 1.3 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.80 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Tensile modulus | 23°C | ISO527-2 | 3500 | Mpa |
| tensile strength | Yield,23°C | ISO527-2 | 60.0 | Mpa |
| elongation | Yield,23°C | ISO527-2 | 5.2 | % |
| Break,23°C | ISO527-2 | 35 | % | |
| Bending modulus | 23°C | ISO178 | 3000 | Mpa |
| bending strength | 23°C | ISO178 | 90.0 | Mpa |
| Poisson's ratio | ISO527-2 | 0.40 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 186 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 65.0 | °C | |
| Melting temperature | ISO3146 | 250 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：23to55°C,2.00mm | ISO11359-2 | 1E-04 | cm/cm/°C | |
| RTIElec | 0.40mm | UL746 | 65.0 | °C |
| 0.75mm | UL746 | 130 | °C | |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| RTI Imp | 0.40mm | UL746 | 65.0 | °C |
| 0.75mm | UL746 | 65.0 | °C | |
| 1.5mm | UL746 | 95.0 | °C | |
| 3.0mm | UL746 | 95.0 | °C | |
| RTIStr | 0.40mm | UL746 | 65.0 | °C |
| 0.75mm | UL746 | 95.0 | °C | |
| 1.5mm | UL746 | 95.0 | °C | |
| 3.0mm | UL746 | 95.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 0.750mm | IEC60093 | 1E+10 | ohms·cm |
| Dielectric strength | 1.00mm | IEC60243 | 26 | KV/mm |
| Arc resistance | 3.00mm | ASTMD495 | PLC6 | |
| Leakage Trace Index | 3.00mm | IEC60112 | 400to599 | V |
| High arc combustion index (HAI) | 0.75mm | UL746 | PLC0 | |
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 | ||
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition (HWI) | 0.75mm | UL746 | PLC0 | |
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40mm | UL94 | V-0 | |
| 0.75mm | UL94 | V-0 | ||
| 1.5mm | UL94 | V-0 | ||
| 2.0mm | UL94 | V-05VA | ||
| 3.0mm | UL94 | V-05VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
| 1.5mm | IEC60695-2-12 | 960 | °C | |
| 3.0mm | IEC60695-2-12 | 960 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 700 | °C |
| 1.5mm | IEC60695-2-13 | 700 | °C | |
| 3.0mm | IEC60695-2-13 | 725 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.