PA6 Zytel® 73G30HSL BK416 DUPONT JAPAN
148
Unit Price:$3074 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.36 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.20 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 6.3 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| MediumDensity | 1.20 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2280 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Bending modulus | ISO178 | 8500 | Mpa | |
| bending strength | ISO178 | 280 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 15 | kJ/m² | |
| Cantilever beam without notch impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
| Tensile modulus | ISO527-2 | 9500 | Mpa | |
| tensile strength | Break | ISO527-2 | 190 | Mpa |
| elongation | Break | ISO527-2 | 3.5 | % |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Multi axis Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 | J |
| Rockwell hardness | R-Scale | ISO2039-2 | 121 | |
| Ball pressure hardness | H961/30 | ISO2039-1 | 230 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 220 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 210 | °C | |
| Glass transition temperature | ISO11357-2 | 60.0 | °C | |
| vicat softening point | ISO306/B50 | 215 | °C | |
| Melting temperature | ISO11357-3 | 221 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | 9.1E-08 | m²/s |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | 50 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | B | ||
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.