PA6 Zytel® 73G30HSL BK416 DUPONT USA
203
Unit Price:$2570 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 187.525MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 密度 | ISO1183 | 1.36 | g/cm³ | |
| 熔体体积流动速率 | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| 收缩率 | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.20 | % | |
| 吸水率 | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % | |
| MeltDensity | 1.20 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2280 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.26 | W/m/K |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸蠕变模量 | 1000hr | ISO899-1 | -- | Mpa |
| 弯曲模量 | ISO178 | 8500 | Mpa | |
| 弯曲强度 | ISO178 | 280 | Mpa | |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 16 | kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 80 | kJ/m² |
| 23°C | ISO179/1eU | 100 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 15 | kJ/m² | |
| 悬臂梁无缺口冲击强度 | 23°C | ISO180/1U | 80 | kJ/m² |
| 拉伸模量 | ISO527-2 | 9500 | Mpa | |
| 拉伸强度 | 断裂 | ISO527-2 | 190 | Mpa |
| 伸长率 | 断裂 | ISO527-2 | 3.5 | % |
| TensileCreepModulus | 1hr | ISO899-1 | -- | Mpa |
| 多轴向仪器化冲击能量 | 23°C | ISO6603-2 | 3.50 | J |
| 洛氏硬度 | R级 | ISO2039-2 | 121 | |
| 球压硬度 | H961/30 | ISO2039-1 | 230 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 210 | °C | |
| 玻璃转化温度 | ISO11357-2 | 60.0 | °C | |
| 维卡软化点 | ISO306/B50 | 215 | °C | |
| 熔融温度 | ISO11357-3 | 221 | °C | |
| 线性热膨胀系数 | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| TD | ISO11359-2 | 7.5E-05 | cm/cm/°C | |
| EffectiveThermalDiffusivity | 9.1E-08 | m²/s |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 燃烧速率 | 1.00mm | ISO3795 | 50 | mm/min |
| UL阻燃等级 | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 极限氧指数 | ISO4589-2 | 21 | % | |
| FMVSS可燃性 | FMVSS302 | B | ||
| 雾化 | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 8.50 | µgC/g | |
| Odor | VDA270 | 3.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.