PA6 Ultramid® B3WG6 BK BASF GERMANY
249
Unit Price:$2855 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Oil resistant Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Automotive sector Engine hood parts Application in the automo
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.36 | g/cm³ | |
| ISO1183 | 1.36 | g/cm³ | ||
| Melt Volume-Flow Rate (MVR) | 275°C/5.0kg | ISO1133 | 40.0 | cm3/10min |
| Shrinkage rate | MD：3.18mm | 0.30 | % | |
| Water absorption rate | Saturation | ASTMD570 | 6.6 | % |
| Saturation,23°C | ISO62 | 6.6 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.1 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 9500 | Mpa |
| tensile strength | Break,23°C | ASTMD638 | 180 | Mpa |
| Break,23°C | ISO527-2 | 180 | Mpa | |
| elongation | Break,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ISO178 | 8300 | Mpa |
| Charpy Notched Impact Strength | -30°C | ISO179 | 9.0 | kJ/m² |
| 23°C | ISO179 | 12 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 65 | kJ/m² |
| 23°C | ISO179 | 80 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 110 | J/m |
| 23°C | ASTMD256 | 150 | J/m | |
| 23°C | ISO180 | 12 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 220 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 210 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Melting temperature | ISO3146 | 220 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.