PA6 Amilan® CM1017XL3 TORAY JAPAN
138
Unit Price:$3243 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 61.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting Low temperature toughness Fast forming cycle
- Application Areas:Automotive sector Shell Electrical components Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：1.00mm3 | % | 0.70到1.1 | -- |
| MD：3.00mm4 | % | 1.2到1.8 | -- | |
| Water absorption rate | 23°C,24hr | % | 1.8 | -- |
| Saturation,23°C | % | 11 | -- | |
| density | ASTM D792/ISO 1183 | 1.13 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.8 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ASTM D785 | 80 | ||
| R-Sale,23°C | 119 | |||
| R-Sale,80°C | 80 | -- | ||
| tensile strength | -40°C | MPa | 110 | |
| 23°C | MPa | 80.0 | 35.0 | |
| 80°C | MPa | 25.0 | 20.0 | |
| elongation | Yield,23°C | % | 1.5 | -- |
| Break,23°C | % | 38 | ||
| Bending modulus | -40°C | MPa | 3800 | 3600 |
| 23°C | MPa | 2800 | ||
| 80°C | MPa | 700 | 300 | |
| bending strength | -40°C | MPa | 135 | |
| 23°C | MPa | 110 | 40.0 | |
| 80°C | MPa | 40.0 | 25.0 | |
| Compressive stress | 23°C | MPa | 80.0 | -- |
| shear strength | 23°C | MPa | 70.0 | 65.0 |
| Taber abraser | 1000Cycles | mg | 3.00到4.00 | -- |
| Friction coefficient vs. Metal | 0.15到0.20 | -- | ||
| Impact strength of simply supported beam without notch | -40°C | 无断裂 | -- | |
| 23°C | 无断裂 | -- |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 182 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 | -- |
| specific heat | J/kg/°C | 1900 | -- | |
| thermal conductivity | W/m/K | 0.25 | -- | |
| melting point | 225 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10^12~13 | Ω.cm | |
| ohms·cm | 1.0E+14到1.0E+15 | 1.0E+11到1.0E+12 | ||
| Dielectric strength | kV/mm | 20 | -- | |
| Dielectric constant | 23°C,50Hz | 4.10 | 9.00 | |
| 23°C,1kHz | 3.90 | 8.00 | ||
| 23°C,1MHz | 3.40 | 4.50 | ||
| Dissipation factor | 23°C,50Hz | 0.070 | 0.10 | |
| 23°C,1kHz | 0.060 | 0.11 | ||
| 23°C,1MHz | 0.030 | 0.13 | ||
| Arc resistance | sec | 120 | -- | |
| Compared to the anti leakage trace index | CTI | V | 600 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.79mm | V-2 | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.