ABS POLYLAC® PA-747H TAIWAN CHIMEI
158
Unit Price:$2129 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 85MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance
- Application Areas:Refrigerator Electrical field Electronic field Electrical appliances
- Color:--
- Grade:Withdrawal level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTMD792 | 1.05 | g/cm³ | |
| Apparent density | ISO60 | 1.05 | g/cm³ | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 0.23 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 2.8 | g/10min | |
| 220°C/10.0kg | ISO1133 | 3.0 | g/10min | |
| Shrinkage rate | ISO294-4 | 0.40到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 屈服 | ISO527-2/50 | 46.0 | Mpa |
| 断裂 | ISO527-2/50 | 35.0 | Mpa | |
| 3.00mm3 | ASTMD638 | 47.1 | Mpa | |
| elongation | 断裂,3.00mm3 | ASTMD638 | 50 | % |
| Impact strength of cantilever beam gap | 23°C,3.00mm | ASTMD256 | 440 | J/m |
| 23°C,6.00mm | ASTMD256 | 310 | J/m | |
| -30°C | ISO180/1A | 22 | kJ/m² | |
| 23°C | ISO180/1A | 33 | kJ/m² | |
| elongation | 断裂 | ISO527-2/50 | 25 | % |
| Bending modulus | 6.00mm4 | ASTMD790 | 2350 | Mpa |
| --5 | ISO178 | 1800 | Mpa | |
| bending strength | 6.00mm4 | ASTMD790 | 68.6 | Mpa |
| --5 | ISO178 | 63.0 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 24 | kJ/m² |
| 23°C | ISO179 | 35 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 101 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8.7E-05 | cm/cm/°C |
| Hot deformation temperature | 1.8MPa,未退火 | ASTMD648 | 85.0 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 84.0 | °C | |
| 1.8MPa,退火 | ASTMD648 | 95.0 | °C | |
| 1.8MPa,退火 | ISO75-2/A | 100 | °C | |
| vicat softening point | -- | ASTMD15256,ISO306/A506 | 106 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.