ABS STAREX® VH-0815T Samsung Cheil South Korea

176

Unit Price:$2800 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 20.5MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact resistance heat-resisting
Application Areas:Automotive components Household appliances
Color:--
Grade:Flame retardant grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD:3.20mm	ISO2577	0.34to0.41	%
Melt mass flow rate	200°C/5.0kg	ASTMD1238	3.8	g/10min
Melt mass flow rate	Melt mass flow rate	200°C/5.0kg	ISO1133	4.2	g/10min
Shrinkage rate	MD：3.20mm	ASTMD955	0.34to0.41	%
	Shrinkage rate	TD：3.20mm	ASTMD955	0.36to0.44	%
	Shrinkage rate	Shrinkage rate	TD:3.20mm	ISO2577	0.36to0.44	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	2000	Mpa
Tensile modulus	Tensile modulus		ISO527-2/50	2200	Mpa
tensile strength	Yield	ASTMD638	39.0	Mpa
	tensile strength	Yield	ISO527-2/50	45.0	Mpa
		tensile strength	Break	ASTMD638	27.0	Mpa
		tensile strength	tensile strength	Break	ISO527-2/50	33.0	Mpa
elongation	Break	ASTMD638	17	%
elongation	elongation	Break	ISO527-2/50	8.0	%
Bending modulus		ASTMD790	2200	Mpa
Bending modulus	Bending modulus		ISO178	2400	Mpa
Bending strength		ASTMD790	59.0	Mpa
Bending strength	bending strength		ISO178	71.0	Mpa
CharpyNotchedImpactStrength	23°C	ISO179/1eA	22	kJ/m²
Suspended wall beam gap impact strength	23°C	ISO180/1A	19	kJ/m²
Rockwell hardness	R-Scale	ASTMD785	100
Rockwell hardness	Rockwell hardness	R-Scale	ISO2039-2	104

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO75-2/B	81.0	°C
	Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO75-2/B	84.0	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTMD648	77.0	°C
			Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO75-2/A	71.0	°C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO75-2/A	79.0	°C
vicat softening point	--	ISO306/B50	86.0	°C
vicat softening point	vicat softening point	--	ISO306/B120	88.0	°C

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	V-1
UL flame retardant rating	UL flame retardant rating	2.0mm	UL94	V-05VB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.