PPS FORTRON® 1140L4 SF3001 CELANESE USA
277
Unit Price:$7256 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 214MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High temperature resistan enhance Glass fiber reinforced Injection grade Medium melt viscosity
- Application Areas:Fiber grade During injection molding Slight flash
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40到0.60 | % |
| MD | ISO294-4 | 0.20到0.60 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.020 | % |
| Density/specific gravity | ISO 1183 | 1.65 | g/cm³ | |
| Water absorption rate | ASTM-D570 | 0.02 | % | |
| Shrinkage rate | ISO 294-4 | 0.2-0.6 | % | |
| density | ASTMD792,ISO1183 | 1.65 | g/cm³ | |
| Specific volume | ASTMD792 | 0.611 | cm³/g | |
| Shrinkage rate | MD | ASTMD955 | 0.20到0.30 | % |
| TD | ASTMD955 | 0.50到0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ISO 527 | 195 | Mpa | |
| Tensile modulus | ISO 527 | 14700 | Mpa | |
| bending strength | ISO 178 | 285 | Mpa | |
| Bending modulus | ISO 178 | 14500 | Mpa | |
| Impact strength of cantilever beam gap | ISO 180/1A | 10 | kJ/m² | |
| Rockwell hardness | ASTM-D785 | 100 | R-Scale | |
| M-Scale | ASTMD785 | 100 | ||
| M-Sale | ISO2039-2 | 100 | ||
| Tensile modulus | -40°C | ASTMD638 | 14500 | Mpa |
| 75°C | ASTMD638 | 11900 | Mpa | |
| 150°C | ASTMD638 | 4270 | Mpa | |
| 200°C | ASTMD638 | 3240 | Mpa | |
| -- | ISO527-2/1A/1 | 14700 | Mpa | |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 10 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Cantilever beam without notch impact strength | 23°C | ISO180/1U | 34 | kJ/m² |
| tensile strength | Break,23°C | ASTMD638 | 200 | Mpa |
| Break | ISO527-2/1A/5 | 195 | Mpa | |
| elongation | Break,23°C | ASTMD638 | 1.7 | % |
| Break | ISO527-2/1A/5 | 1.9 | % | |
| Bending modulus | 23°C | ISO178 | 14500 | Mpa |
| Bending stress | ISO178 | 285 | Mpa | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 53 | kJ/m² |
| 23°C | ISO179/1eU | 53 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 4.2E-05 | cm/cm/°C |
| Hot deformation temperature | 0.45MPa,Annealed | ASTMD648 | 280 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 265 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 270 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 215 | °C | |
| Glass transition temperature | ISO11357-2 | 90.0 | °C | |
| Melting temperature | ISO11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| Hot deformation temperature | 1.80Mpa | ISO 75-A | 270 | °C |
| Flame retardant grade | UL94 | V-0 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1MHz | IEC60250 | 6.2E-03 | |
| Arc resistance | ASTMD495 | 134 | sec | |
| Leakage Trace Index | IEC60112 | 125 | V | |
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | -- | ASTMD257 | 1E+16 | ohms·cm |
| -- | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 28 | KV/mm | |
| Dielectric constant | 1kHz | ASTMD150 | 3.50 | |
| 1MHz | ASTMD150 | 3.50 | ||
| 1MHz | IEC60250 | 4.60 | ||
| Dissipation factor | 1kHz | ASTMD150 | 1E-03 | |
| 1MHz | ASTMD150 | 1E-03 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| SpecificHeatCapacity of Melt | 内部方法 | 1500 | J/kg/°C |
| Biochemical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling amount | 40 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.38mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-0 | ||
| 3.0mm | UL94 | 5VA | ||
| Extreme Oxygen Index | ISO4589-2 | 47 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| SpecimensThickness Shrinkage | 内部方法 | 3.18 | mm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.