LCP VECTRA® E130i-BK210P CELANESE USA
303
Unit Price:$8748 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 201MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting Flame retardant enhance
- Application Areas:Household appliances Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.40 | % |
| MD | ISO294-4 | 0.10 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.030 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | 23°C | ISO180/1U | 31 | kJ/m² |
| Tensile modulus | ISO527-2/1A/1 | 15000 | Mpa | |
| tensile strength | Break | ISO527-2/1A/5 | 150 | Mpa |
| elongation | Break | ISO527-2/1A/5 | 1.6 | % |
| Rockwell hardness | M-Scale | ISO2039-2 | 71 | |
| Bending modulus | 23°C | ISO178 | 13500 | Mpa |
| bending strength | 23°C | ISO178 | 220 | Mpa |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 43 | kJ/m² |
| Compressive modulus | ISO604 | 14000 | Mpa | |
| CompressiveStress | 1%Strain | ISO604 | 93.0 | Mpa |
| Fracture bending strain | ISO178 | 2.2 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 276 | °C |
| 8.0MPa,Unannealed | ISO75-2/C | 216 | °C | |
| Melting temperature | ISO11357-3 | 335 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 7E-06 | cm/cm/°C |
| TD | ISO11359-2 | 2E-05 | cm/cm/°C | |
| vicat softening point | ISO306/B50 | 195 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Arc resistance | 内部方法 | 140 | sec | |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Relative permittivity | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.30 | ||
| 2.05GHz | 内部方法 | 4.23 | ||
| Leakage Trace Index | IEC60112 | 175 | V | |
| Dissipation factor | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.025 | ||
| 2.05GHz | 内部方法 | 6E-03 | ||
| Dielectric strength | IEC60243-1 | 32 | KV/mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | V-0 | ||
| Extreme Oxygen Index | ISO4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.