POM HOSTAFORM® M270NAT CELANESE USA
157
Unit Price:$2384 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low molecular weight Good forming performance High mobility
- Application Areas:Household appliances Household appliances Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 2.2 | % |
| TD | ASTMD955 | 1.8 | % | |
| TD | ISO294-4 | 1.6 | % | |
| MD | ISO294-4 | 1.7 | % | |
| SpecificHeatCapacity of Melt | 内部方法 | 2210 | J/kg/°C | |
| ThermalConductivityofMelt | 内部方法 | 0.16 | W/m/K | |
| Melt Volume-Flow Rate (MVR) | 190°C/2.16kg | ISO1133 | 23.0 | cm3/10min |
| Water absorption rate | Saturation,23°C | ISO62 | 0.75 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.20 | % | |
| Density of Melt | 内部方法 | 1.200 | g/cm³ | |
| density | ISO1183 | 1.41 | g/cm³ | |
| ASTMD792 | 1.41 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| TensileCreepModule | 1hr | ISO899-1 | 2300 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.2 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 5.4 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 110 | kJ/m² |
| 23°C | ISO179/1eU | 120 | kJ/m² | |
| Tensile creep modulus | 1000hr | ISO899-1 | 1300 | Mpa |
| Tensile modulus | ISO527-2/1A/1 | 2800 | Mpa | |
| tensile strength | Yield,23°C | ASTMD638 | 60.7 | Mpa |
| Yield | ISO527-2/1A/50 | 67.0 | Mpa | |
| elongation | Yield | ISO527-2/1A/50 | 8.0 | % |
| Bending modulus | 23°C | ISO178 | 2750 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 156 | °C |
| 1.8MPa,Unannealed | ASTMD648 | 110 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 103 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| TD | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| Melting temperature | ISO11357-3 | 166 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.