PPO FLEX NORYL™ GFN1V-GY4461 SABIC INNOVATIVE US
126
Unit Price:$3736 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Hydrolysis resistance
- Application Areas:Automotive components Laptop case
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 300°C/5.0kg | ISO1133 | 16.4 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.20to0.50 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Outdoor applicability | UL746C | f1 | ||
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 17 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 21.7 | J |
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 9.4 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | 25 | kJ/m² |
| 23°C | ISO180/1U | 28 | kJ/m² | |
| Simple supported beam without notch impact strength | -30°C | ISO179/1eU | 33 | kJ/m² |
| 23°C | ISO179/1eU | 35 | kJ/m² | |
| Tensile modulus | ASTMD638 | 4350 | Mpa | |
| ISO527-2/1 | 4400 | Mpa | ||
| tensile strength | Break | ASTMD638 | 63.0 | Mpa |
| Break | ISO527-2 | 64.0 | Mpa | |
| elongation | Break | ASTMD638 | 3.0 | % |
| Break | ISO527-2 | 3.0 | % | |
| Rockwell hardness | L-Sale | ASTMD785 | 104 | |
| Bending modulus | 50.0mmSpan4 | ASTMD790 | 3840 | Mpa |
| 100mmSpan5 | ASTMD790 | 3590 | Mpa | |
| ISO178 | 4160 | Mpa | ||
| bending strength | ISO178 | 122 | Mpa | |
| Yield,50.0mmSpan4 | ASTMD790 | 116 | Mpa | |
| Yield,100mmSpan5 | ASTMD790 | 108 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B50 | 131 | °C |
| -- | ISO306/B120 | 134 | °C | |
| RTIElec | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 5.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 7.1E-05 | cm/cm/°C | |
| RTI Imp | UL746 | 90.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 131 | °C |
| 0.45MPa,Unannealed,100mmSpan | ISO75-2/Be | 132 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 122 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 125 | °C | |
| 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 124 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC5 | |
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC4 | |
| Dissipation factor | 1MHz | ASTMD150 | 1.4E-03 | |
| Dielectric constant | 1MHz | ASTMD150 | 2.90 | |
| Arc resistance | ASTMD495 | PLC7 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.