PPO NORYL™ N190X-701 SABIC INNOVATIVE SHANGHAI
241
Unit Price:$3490 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:transparent High temperature resistan
- Application Areas:Automotive components Illuminating lamp
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 280°C/5.0 kg | ASTM D1238 | 20 | g/10 min |
| Melt Volume-Flow Rate (MVR) | 280°C/5.0 kg | ISO 1133 | 23.0 | cm3/10min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.080 | % |
| Outdoor applicability | UL 746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 | |
| Tensile modulus | -- 2 | ASTM D638 | 2580 | Mpa |
| -- | ISO 527-2/1 | 2600 | Mpa | |
| tensile strength | Yield 3 | ASTM D638 | 60.0 | Mpa |
| Yield | ISO 527-2/50 | 58.0 | Mpa | |
| Break 3 | ASTM D638 | 47.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| elongation | Yield 3 | ASTM D638 | 3.6 | % |
| Yield | ISO 527-2/50 | 3.2 | % | |
| Break 3 | ASTM D638 | 9.0 | % | |
| Break | ISO 527-2/50 | 9.2 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2500 | Mpa |
| 100 mm Span 5 | ASTM D790 | 2300 | Mpa | |
| -- 6 | ISO 178 | 2350 | Mpa | |
| bending strength | -- 6, 7 | ISO 178 | 87.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 98.0 | Mpa | |
| Yield, 100 mm Span 5 | ASTM D790 | 91.0 | Mpa | |
| Taber abraser | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 76.0 | mg |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 720 | J/m |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 50.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 95.0 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Bf | 95.0 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 78.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 86.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 8 | ISO 75-2/Af | 82.0 | °C | |
| vicat softening point | -- | ASTM D15259 | 104 | °C |
| -- | ISO 306/B120 | 107 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 7.7E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 8.1E-5 | cm/cm/°C | |
| thermal conductivity | ASTM C177 | 0.24 | W/m/K | |
| RTI Elec | UL 746 | 95.0 | °C | |
| RTI Imp | UL 746 | 80.0 | °C | |
| RTI | UL 746 | 95.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.8E+16 | ohms·cm | |
| Dielectric strength | 3.20 mm, in Oil | ASTM D149 | 19 | KV/mm |
| Dielectric constant | 100 Hz | ASTM D150 | 2.74 | |
| 100 kHz | ASTM D150 | 2.60 | ||
| Dissipation factor | 100 Hz | ASTM D150 | 0.013 | |
| 100 kHz | ASTM D150 | 5.5E-3 | ||
| Arc resistance | ASTM D495 | PLC 7 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | ||
| High arc combustion index (HAI) | UL 746 | PLC 2 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 2 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 75 到 80 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 215 到 265 | °C | ||
| Temperature in the middle of the barrel | 225 到 270 | °C | ||
| Temperature at the front of the material cylinder | 240 到 275 | °C | ||
| Spray nozzle temperature | 250 到 275 | °C | ||
| Processing (melt) temperature | 250 到 275 | °C | ||
| Mold temperature | 55 到 75 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.0 mm | UL 94 | HB | |
| 1.5 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA | ||
| Extreme Oxygen Index | ASTM D2863 | 39 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.