PPO NORYL™ GFN3-701 SABIC INNOVATIVE NANSHA
239
Unit Price:$3834 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 35MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced Hydrolysis resistance
- Application Areas:Lawn equipment Garden equipment Non specific food Outdoor applications Electrical field Electronic field Architectural application Liquid handling Electrical appliances Engine hood parts Medical supplies Nursing supplies Plastic bag Automotive External Parts Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 8.7 | g/10min |
| Melt Volume-Flow Rate (MVR) | 300°C/5.0kg | ISO1133 | 7.82 | cm3/10min |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10to0.40 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 9150 | Mpa | |
| ISO527-2/1 | 8740 | Mpa | ||
| tensile strength | Break | ASTMD638 | 116 | Mpa |
| Break | ISO527-2 | 117 | Mpa | |
| elongation | Break | ASTMD638 | 2.0 | % |
| Break | ISO527-2 | 1.8 | % | |
| Bending modulus | 100mmSpan4 | ASTMD790 | 7170 | Mpa |
| 50.0mmSpan5 | ASTMD790 | 8000 | Mpa | |
| ISO178 | 8710 | Mpa | ||
| bending strength | ISO178 | 183 | Mpa | |
| Yield,50.0mmSpan5 | ASTMD790 | 180 | Mpa | |
| Yield,100mmSpan4 | ASTMD790 | 162 | Mpa | |
| Simple supported beam without notch impact strength | -30°C | ISO179/1eU | 47 | kJ/m² |
| 23°C | ISO179/1eU | 39 | kJ/m² | |
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 12 | kJ/m² |
| 23°C | ISO180/1A | 12 | kJ/m² | |
| Unscented Izod Impact Strength | -30°C | ISO180/1U | 36 | kJ/m² |
| 23°C | ISO180/1U | 32 | kJ/m² | |
| Rockwell hardness | L-Sale | ASTMD785 | 108 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIElec | UL746 | 90.0 | °C | |
| RTI Imp | UL746 | 90.0 | °C | |
| RTIStr | UL746 | 90.0 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 142 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 158 | °C | |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 143 | °C | |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 137 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 138 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 137 | °C | |
| vicat softening point | -- | ISO306/B50 | 143 | °C |
| -- | ISO306/B120 | 147 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 3.1E-05 | cm/cm/°C |
| TD：-40to40°C | ASTME831 | 6.2E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 3.20mm,inOil | ASTMD149 | 22 | KV/mm |
| Dielectric constant | 50Hz | ASTMD150 | 2.93 | |
| 60Hz | ASTMD150 | 2.93 | ||
| Dissipation factor | 50Hz | ASTMD150 | 9E-04 | |
| 60Hz | ASTMD150 | 9E-04 | ||
| Arc resistance | ASTMD495 | PLC7 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 | |
| High arc combustion index | HAI | UL746 | PLC4 | |
| High voltage arc tracing rate | HVTR | UL746 | PLC3 | |
| Hot wire ignition | HWI | UL746 | PLC4 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| Extreme Oxygen Index | ASTMD2863 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.