PBT/ASA Ultradur® S4090G6 BASF GERMANY
233
Unit Price:$3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 71MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Aging resistance Antichemical Dimensional stability high strength Weather resistance
- Application Areas:Automotive sector Industrial components Electronic field Electrical field Applied in fields that re As for the load-bearing p
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO 1183 | 1.47 | g/cm | |
| Water absorption rate | 0.4 | % | ||
| Melt mass flow rate | ISO 1133 | 20 | cm ³ /10min | |
| Shrinkage rate | Across Flow | 0.1 | % | |
| Across Flow | 0.75 | % | ||
| density | ISO 1183 | 1.39 | g/cm³ | |
| Melt mass flow rate | ISO 1133 | 20 | cm3/10min | |
| Water absorption rate | 0.4 | % | ||
| Shrinkage rate | Across Flow | 0.16 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus of elasticity | ISO 527-1/-2 | 6900 | Mpa | |
| tensile strength | ISO 527-1/-2 | 100 | Mpa | |
| elongation | Break | 2.5 | % | |
| bending strength | ISO 178 | 151 | Mpa | |
| Impact strength of simply supported beam without notch | 23 ℃ | 55 | kJ/m² | |
| Impact strength of simply supported beam gap | 7 | kJ/m² | ||
| ball indentation hardness | ISO 2039-1 | 153 | Mpa | |
| Tensile modulus of elasticity | 9700 | Mpa | ||
| elongation | Break | ISO 527-1/- 2 | 2.2 | % |
| bending strength | ISO 178 | 183 | Mpa | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eU | 59 | KJ/m |
| Impact strength of simply supported beam gap | 23℃ | ISO 179/1eA | 9 | KJ/m |
| ball indentation hardness | ISO 2039-1 | 164 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility | UL94 | HB | ||
| Hot deformation temperature | 1.80 MPa | ISO 75-1/-2 | 175 | °C |
| 0.45 MPa | ISO 75-1/-2 | 210 | °C | |
| Combustibility | UL94 | HB | ||
| Hot deformation temperature | 1.80 MPa | 160 | °C | |
| Linear coefficient of thermal expansion | ISO 11359-1/-2 | 0.4 | E-4/°C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fiberglass content | 20 | % |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 250-270 | °C | ||
| Mold temperature | 60-100 | °C | ||
| Melt Temperature | 250-275 | °C | ||
| Mold temperature | 60-100 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fiberglass content | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.