PARA IXEF® 1622/9708 SOLVAY USA
219
Unit Price:$7424 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength Creep resistance Filler: Glass fiber reinf 50% filler by weight
- Application Areas:Automotive interior parts sporting goods Vehicle electronics Lawn and garden equipment Application in the automo Business equipment Power/Other Tools Home appliance components Industrial applications furniture Electrical enclosure Engine parts Camera applications Electrical appliances Shell Metal substitution Machine/mechanical compon
- Color:--
- Grade:Coating grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 275°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.04 | |
| -- | 1.36到1.82 | |||
| Saturation, 23 ℃ | % | 0.060到0.15 | ||
| Balance, 23 ℃, 50% RH | % | 0.70到1.5 | ||
| 23℃ | % | 0.19到0.40 | ||
| g/cm³ | 1.43到1.77 | |||
| 23℃,24hr | % | 0.16到0.30 | ||
| Flow: 23 ℃ | mm/mm | 38.1E-3到78.7E-3 | ||
| Melt mass flow rate | 275°C/2.16kg | g/10min | 3.6到20 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 23℃ | MPa | 280.0到402.07 | ||
| MPa | 11931.03到24896.55 | |||
| MPa | 7586.21到23448.28 | |||
| MPa | 8482.76到21379.31 | |||
| MPa | 141.38到268.97 | |||
| MPa | 11517.24到23517.24 | |||
| MPa | 203.45到389.66 | |||
| Fracture, 23 ℃ | % | 1.6到2.1 | ||
| MPa | 151.72到280.69 | |||
| Yield, 23 ℃ | % | 2.0到3.0 | ||
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.647到20.893 | |
| Cantilever beam without notch impact strength | 23℃ | J/m | 0.222到0.332 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0.45MPa, unannealed | °C | 234到255 | ||
| 1.8MPa, unannealed | °C | 223到230 | ||
| transverse | mm/mm/°C | 55.9E-5到50.8E-5 | ||
| flow | mm/mm/°C | 137.2E-5到25.4E-5 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Leakage Trace Index | V | 320到600 | ||
| Surface resistivity | ohms | 5.0E+3到6.0E+15 | ||
| Volume resistivity | 23℃ | ohms·cm | 3.0E+2到2.1E+16 | |
| Dielectric strength | 23℃ | V/mil | 500到840 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | °C | 798到904 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.