PPO/PA NORYL GTX™ GTX810-111 SABIC INNOVATIVE US
249
Unit Price:$5820 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 26MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance enhance High temperature resistan
- Application Areas:Casters fibre
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.60 到 0.80 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.65 到 0.85 | % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.50 | % |
| Equilibrium, 50% RH | ASTM D570 | 1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 119 | |
| Tensile strength | Yield | ASTM D638 | 89.0 | Mpa |
| Break | ASTM D638 | 88.0 | Mpa | |
| elongation | Break | ASTM D638 | 10 | % |
| Bending modulus | 100 mm Span | ASTM D790 | 3960 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 155 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 245 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 210 | °C | |
| vicat softening point | ASTM D15253 | 240 | °C | |
| Linear coefficient of thermal expansion - flow | -20 to 150°C | ASTM E831 | 4.0E-5 到 5.0E-5 | cm/cm/°C |
| RTI Elec | UL 746 | 50.0 | °C | |
| RTI Imp | UL 746 | 50.0 | °C | |
| RTI | UL 746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTM D495 | PLC 6 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 3 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 95 到 105 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.070 | % | ||
| Suggested injection volume | 30 到 50 | % | ||
| Temperature at the rear of the barrel | 265 到 305 | °C | ||
| Temperature in the middle of the barrel | 270 到 305 | °C | ||
| Temperature at the front of the material cylinder | 275 到 305 | °C | ||
| Spray nozzle temperature | 280 到 305 | °C | ||
| Processing (melt) temperature | 280 到 305 | °C | ||
| Mold temperature | 75 到 120 | °C | ||
| Back pressure | 0.300 到 1.40 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.013 到 0.038 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App