ASA/PC GELOY™ HRA222F SABIC INNOVATIVE US
271
Unit Price:$3339 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 105MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Thermal stability
- Application Areas:Home appliance components Lawn garden equipment
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体体积流动速率 | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
| 收缩率 - 流动 | 内部方法 | 0.40 到 0.60 | % | |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.60 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| 室外适用性 | UL 746C | f1 |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | -- 3 | ASTM D638 | 2590 | Mpa |
| -- | ISO 527-2/1 | 2520 | Mpa | |
| 拉伸强度 | 屈服 4 | ASTM D638 | 63.0 | Mpa |
| 屈服 5 | ASTM D638 | 59.0 | Mpa | |
| 屈服 | ISO 527-2/5 | 62.0 | Mpa | |
| 屈服 | ISO 527-2/50 | 60.0 | Mpa | |
| 断裂 5 | ASTM D638 | 66.0 | Mpa | |
| 断裂 4 | ASTM D638 | 56.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 51.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 | Mpa | |
| 伸长率 | 屈服 5 | ASTM D638 | 4.2 | % |
| 屈服 4 | ASTM D638 | 4.3 | % | |
| 屈服 | ISO 527-2/5 | 4.3 | % | |
| 屈服 | ISO 527-2/50 | 4.4 | % | |
| 断裂 5 | ASTM D638 | > 100 | % | |
| 断裂 4 | ASTM D638 | > 100 | % | |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
| 弯曲模量 | ISO 178 | 2510 | Mpa | |
| 弯曲应力 6, | ISO 178 | 93.0 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 | °C | |
| 维卡软化点 | -- | ISO 306/A50 | 111 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 104 | °C | |
| Ball Pressure Test | 73 到 77°C | IEC 60695-10-2 | 通过 | |
| 线性热膨胀系数 | 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
| 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI | UL 746 | 90.0 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 0 | ||
| 漏电起痕指数 | IEC 60112 | 600 | V |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 到 90 | °C | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 料斗温度 | 60 到 80 | °C | ||
| 料筒后部温度 | 200 到 230 | °C | ||
| 料筒中部温度 | 220 到 260 | °C | ||
| 料筒前部温度 | 230 到 270 | °C | ||
| 射嘴温度 | 220 到 260 | °C | ||
| 加工（熔体）温度 | 230 到 270 | °C | ||
| 模具温度 | 50 到 70 | °C |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 2.0 mm | UL 94 | V-0 | |
| 极限氧指数 | ISO 4589-2 | 29 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.