SPS XAREC™ C132 IDEMITSU JAPAN
245
Unit Price:$8036 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced High temperature resistan
- Application Areas:Household goods
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 | ||
| Shrinkage rate | ASTM D955 | MD 0.1～0.4 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.01 | % | |
| Shrinkage rate | TD | 内部方法 | 0.50to0.80 | % |
| MD | 内部方法 | 0.10to0.40 | % | |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.010 | % |
| 0.05 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 9700 | Mpa | |
| tensile strength | Break | ISO527-2 | 120 | Mpa |
| elongation | Break | ISO527-2 | 2.1 | % |
| Bending modulus | ISO178 | 9200 | Mpa | |
| bending strength | ISO178 | 185 | Mpa | |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 43 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO180 | 36 | kJ/m² |
| elongation at break | ASTM D638/ISO 527 | 2.1 | % | |
| tensile strength | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 70 | ||
| Bending modulus | ASTM D790/ISO 178 | 9.2 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 185 | kg/cm²(MPa)[Lb/in²] | |
| Flexural strength | 165 | Mpa | ||
| Flexural modulus of elasticity | 8100 | Mpa | ||
| Tensile strength | 105 | Mpa | ||
| elongation | Break | 2.3 | % | |
| IZOD impact strength | 4mm 有Notch | 10 | KJ/m | |
| 3.2mm 没有Notch | 40 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB/0.80 | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | MD 1.8 | mm/mm.℃ | |
| Combustibility | 1/32英寸 | UL 94 | HB | |
| Hot deformation temperature | 235 | °C | ||
| 0.45MPa,Unannealed | ISO75-2/B | 265 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 240 | °C | |
| Linear coefficient of thermal expansion | MD：-30to30°C | TMA | 1.8E-05 | cm/cm/°C |
| TD：-30to30°C | TMA | 3.9E-05 | cm/cm/°C | |
| RTIElec | UL746 | 50.0 | °C | |
| RTI Imp | UL746 | 50.0 | °C | |
| RTIStr | UL746 | 50.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+16 | ohms·cm | |
| Dielectric strength | ASTMD149 | 45 | KV/mm | |
| Dielectric constant | 1MHz | IEC60250 | 2.90 | |
| Dissipation factor | 1MHz | IEC60250 | <1.0E-3 | |
| Arc resistance | ASTMD495 | PLC6 | ||
| Compared to the anti leakage trace index | CTI)3 | IEC60112 | PLC1 | |
| Arc resistance | ASTM D495/IEC 60112 | 120 | ||
| Volume resistivity | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | >0.75mm | UL94 | HB |
| Processing conditions | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | 0.35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.