PC/PBT XENOY™ 6370-8A6D030 SABIC INNOVATIVE US
141
Unit Price:$3112 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 83MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Low temperature impact re
- Application Areas:Household daily necessiti Electrical applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/5.0kg | ASTMD1238 | 24 | g/10min |
| Melt Volume-Flow Rate (MVR) | 250°C/5.0kg | ISO1133 | 12.0 | cm3/10min |
| 265°C/5.0kg | ISO1133 | 19.0 | cm3/10min | |
| Shrinkage rate | MD：--2 | 内部方法 | 0.30to0.40 | % |
| MD：--3 | 内部方法 | 0.40to0.50 | % | |
| TD：--2 | 内部方法 | 0.40to0.70 | % | |
| TD：--3 | 内部方法 | 0.70to0.90 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.090 | % |
| Saturation,23°C | ISO62 | 0.50 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Specific volume | ASTMD792 | 0.700 | cm³/g |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,EnergyatPeakLoad | ASTMD3763 | 5.00 | J |
| 23°C,TotalEnergy | ASTMD3763 | 17.0 | J | |
| Rockwell hardness | R-Scale | ASTMD785 | 109 | |
| Bending modulus | 50.0mmSpan | ASTMD790 | 5380 | Mpa |
| ISO178 | 7750 | Mpa | ||
| Bending strength 7, | ISO178 | 154 | Mpa | |
| Bending strength | Yield,50.0mmSpan | ASTMD790 | 150 | Mpa |
| FlexuralStrength | Break,50.0mmSpan | ASTMD790 | 138 | Mpa |
| CharpyNotchedImpactStrength | 23°C | ISO179/1eA | 9.0 | kJ/m² |
| Suspended wall beam gap impact strength | -30°C | ISO180/1A | 6.0 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² | |
| Tensile modulus | ASTMD638 | 9750 | Mpa | |
| ISO527-2/1 | 8500 | Mpa | ||
| Tensile strength | Yield | ASTMD638 | 97.0 | Mpa |
| tensile strength | Yield | ISO527-2/5 | 105 | Mpa |
| Break | ASTMD638 | 91.0 | Mpa | |
| Break | ISO527-2/5 | 3.00 | Mpa | |
| Tensile strain | Yield | ASTMD638 | 3.0 | % |
| elongation | Yield | ISO527-2/5 | 3.0 | % |
| Tensile strain | Break | ASTMD638 | 4.0 | % |
| elongation | Break | ISO527-2/5 | 110 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | -- | ISO306/B120 | 150 | °C |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.7E-05 | cm/cm/°C |
| MD：60to138°C | ASTME831 | 2E-05 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 2.7E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| RTIElec | UL746 | 140 | °C | |
| RTI Imp | UL746 | 130 | °C | |
| RTIStr | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 204 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 163 | °C | |
| 1.8MPa,Unannealed,6.40mm | ASTMD648 | 149 | °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 155 | °C | |
| vicat softening point | ASTMD152512 | 153 | °C | |
| -- | ISO306/B50 | 148 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 1.60mm,in Oil | ASTMD149 | 27 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 20 | KV/mm | |
| Dielectric constant | 100Hz | ASTMD150 | 4.00 | |
| 1MHz | ASTMD150 | 4.00 | ||
| Dissipation factor | 100Hz | ASTMD150 | 3E-03 | |
| 1MHz | ASTMD150 | 0.020 | ||
| Arc resistance | ASTMD495 | PLC5 | ||
| Compared to the anti leakage trace index | CTI | UL746 | PLC2 | |
| High arc combustion index | HAI | UL746 | PLC3 | |
| HAI | UL746 | PLC3 | ||
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition | HWI | UL746 | PLC1 | |
| Volume resistivity | ASTMD257 | 4.8E+15 | ohms·cm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.