TPEE Hytrel® 8238 DUPONT USA
252
Unit Price:$7399 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Aging resistance
- Application Areas:Casters medical care
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 密度 | ISO1183 | 1.28 | g/cm³ | |
| 熔体质量流动速率 | 240°C/2.16kg | ISO1133 | 13 | g/10min |
| 熔体体积流动速率 | 240°C/2.16kg | ISO1133 | 11.5 | cm3/10min |
| 收缩率 | TD | ISO294-4 | 1.6 | % |
| MD | ISO294-4 | 1.6 | % | |
| 吸水率 | 23°C,24hr | ISO62 | 0.30 | % |
| 饱和,23°C,2.00mm | ISO62 | 0.60 | % | |
| 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MeltDensity | 1.13 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | ISO527-2 | 1200 | Mpa | |
| 简支梁缺口冲击强度 | -40°C | ISO179/1eA | 5.0 | kJ/m² |
| -30°C | ISO179/1eA | 5.0 | kJ/m² | |
| 23°C | ISO179/1eA | 15 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -40°C | ISO180/1A | 5.5 | kJ/m² |
| 23°C | ISO180/1A | 11 | kJ/m² | |
| 拉伸冲击强度 | 23°C | ISO8256/1 | 57.0 | kJ/m² |
| 肖氏硬度 | 邵氏D | ISO868 | 76 | |
| 邵氏D,15秒 | ISO868 | 70 | ||
| 拉伸强度 | 屈服 | ISO527-2 | 38.0 | Mpa |
| 断裂 | ISO527-2 | 46.0 | Mpa | |
| 10%应变 | ISO527-2 | 34.0 | Mpa | |
| 50%应变 | ISO527-2 | 28.0 | Mpa | |
| 100%应变 | ISO527-2 | 26.0 | Mpa | |
| 伸长率 | 屈服 | ISO527-2 | 19 | % |
| 断裂 | ISO527-2 | >300 | % | |
| 标称拉伸断裂应变 | ISO527-2 | 340 | % | |
| 弯曲模量 | ISO178 | 1150 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 线性热膨胀系数 | TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/B | 105 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 45.0 | °C | |
| 脆化温度 | ISO974 | -84.0 | °C | |
| 玻璃转化温度 | ISO11357-2 | 50.0 | °C | |
| 维卡软化点 | -- | ISO306/A50 | 213 | °C |
| -- | ISO306/B50 | 150 | °C | |
| 熔融温度 | ISO11357-3 | 221 | °C | |
| 线性热膨胀系数 | MD：-- | ISO11359-2 | 1.5E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.4E-04 | cm/cm/°C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC60093 | >1.0E+15 | ohms | |
| 体积电阻率 | IEC60093 | >1.0E+15 | ohms·cm | |
| 介电强度 | IEC60243-1 | 21 | KV/mm | |
| 相对电容率 | 100Hz | IEC60250 | 4.00 | |
| 1MHz | IEC60250 | 3.70 | ||
| 耗散因数 | 100Hz | IEC60250 | 0.010 | |
| 1MHz | IEC60250 | 0.018 | ||
| 漏电起痕指数 | IEC60112 | 600 | V |
| 弹性体 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 撕裂强度 | 横向流量 | ISO34-1 | 210 | kN/m |
| 流量 | ISO34-1 | 230 | kN/m |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL阻燃等级 | 0.9mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.9mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 极限氧指数 | ISO4589-2 | 22 | % | |
| FMVSS可燃性 | FMVSS302 | SE |
| 补充信息 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 550 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.