Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability
- Application Areas:Pipeline components sheet Electric wire Cable Applications Industrial applications Automotive sector Filamentous Fitness equipment Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.22 | g/cm³ | |
| Melt mass flow rate | 230°C/2.16kg | ISO1133 | 9.0 | g/10min |
| Melt Volume-Flow Rate (MVR) | 230°C/2.16kg | ISO1133 | 8.50 | cm3/10min |
| Shrinkage rate | TD | ISO294-4 | 1.5 | % |
| MD | ISO294-4 | 1.5 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Saturation,23°C,2.00mm | ISO62 | 0.60 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.06 | g/cm³ | ||
| SpecificHeatCapacity of Melt | 2150 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.15 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -40°C | ISO179/1eA | 15 | kJ/m² |
| -30°C | ISO179/1eA | 25 | kJ/m² | |
| 23°C,Partial Break | ISO179/1eA | 120 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 19 | kJ/m² |
| 23°C | ISO180/1A | 81 | kJ/m² | |
| Tensile modulus | ISO527-2 | 280 | Mpa | |
| tensile strength | Yield | ISO527-2 | 20.0 | Mpa |
| Bending modulus | ISO178 | 290 | Mpa | |
| abrasion resistance | ISO4649 | 110 | mm³ | |
| Tensile impact strength | 23°C | ISO8256/1 | 300 | kJ/m² |
| Shore hardness | Shore D | ISO868 | 63 | |
| Shore D,15sec | ISO868 | 57 | ||
| tensile strength | Break | ISO527-2 | 43.0 | Mpa |
| 5.0%Strain | ISO527-2 | 12.0 | Mpa | |
| 10%Strain | ISO527-2 | 15.0 | Mpa | |
| 50%Strain | ISO527-2 | 18.8 | Mpa | |
| 100%Strain | ISO527-2 | 19.0 | Mpa | |
| elongation | Yield | ISO527-2 | 31 | % |
| Break | ISO527-2 | >300 | % | |
| Nominal tensile fracture strain | ISO527-2 | 500 | % | |
| TensileCreepModule | 1hr | ISO899-1 | 248 | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | 182 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 1.9E-04 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 1.6E-04 | cm/cm/°C | |
| TD：23to55°C | ASTME831 | 1.7E-04 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 1.8E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 5.44E-08 | m²/s | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 80.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 45.0 | °C | |
| Brittle temperature | ISO974 | -96.0 | °C | |
| Glass transition temperature | ISO11357-2 | 0.00 | °C | |
| vicat softening point | -- | ISO306/A50 | 195 | °C |
| -- | ISO306/B50 | 100 | °C | |
| Melting temperature | ISO11357-3 | 210 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 1MHz | IEC60250 | 4.10 | |
| Dissipation factor | 100Hz | IEC60250 | 0.012 | |
| 1MHz | IEC60250 | 0.036 | ||
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | 8E+13 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 20 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.60 |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tear strength | Across Flow | ISO34-1 | 150 | kN/m |
| 流量 | ISO34-1 | 160 | kN/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| 3.0mm | UL94 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| 3.0mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 21 | % | |
| FMVSS flammability | FMVSS302 | SE | ||
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 2.50 | µgC/g | |
| Odor | VDA270 | 2.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.