TPEE KEYFLEX® BT-1155D LG CHEM KOREA
199
Unit Price:$5947 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Processability Good stability
- Application Areas:Electric wire Cable Automotive sector sporting goods Application in the automo Pipe fittings pipeline Wire and cable applicatio Cable sheath
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 230℃/2.16Kg | ASTMD1238 | 25 | g/10min |
| 230°C/2.16kg | ASTMD1238 | 14 | g/10min | |
| Shrinkage rate | MD：3.20mm,InjectionMolded | ASTMD955 | 1.0to1.4 | % |
| Water absorption rate | 23°C,24hr | ASTMD570 | 0.60 | % |
| Shrinkage rate | MD | ASTMD995 | 1.1-1.5 | % |
| Water absorption rate | (23°C,24hr) | ASTMD570 | 0.6 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,23°C,2.00mm,InjectionMolded | ASTMD638 | 13.2 | Mpa |
| Shaw Brothers A | ASTMD2240 | 55 | ||
| tensile strength | 23°C | ASTMD638 | 13 | Mpa |
| elongation at break | 23°C | ASTMD638 | 800 | % |
| Bending modulus | 23°C | ASTMD790 | 196 | Mpa |
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | NB | J/m |
| -40°C | ASTMD256 | 150 | J/m | |
| tensile strength | Break,23°C,2.00mm,Injection | ASTMD638 | 34.3 | Mpa |
| elongation | Break,23°C,2.00mm,Injection | ASTMD638 | 850 | % |
| Bending modulus | 23°C,6.40mm,InjectionMolded | ASTMD790 | 167 | Mpa |
| DurometerHardness | ShoreD,23°C,InjectionMolded | ASTMD2240 | 52 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm,Injection | ASTMD648 | 85.0 | °C |
| Peak melting temperature | ASTMD3418 | 200 | °C | |
| Hot deformation temperature | 0.45MPaUnannealed | ASTMD648 | 90 | °C |
| vicat softening point | Melting Temperature | ASTMD3418 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | ASTMD257 | >E13 | Ω.cm | |
| Volume resistivity | 23°C | ASTMD257 | >1.0E+13 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | ASTMD149 | 26 | KV/mm |
| Leakage Trace Index | SolutionA | IEC60112 | 600 | V |
| Insulation strength | ASTMD149 | 26 | KV/mm |
| elastomer | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tear strength | 23°C | ASTMD624 | 147 | kN/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.