PPA AMODEL® A-1145HS BK324 SOLVAY USA
264
Unit Price:$7468 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance｜Low moisture absorption｜Filler: Glass fiber reinf｜45% filler by weight
- Application Areas:Shell｜Vehicle electronics｜Industrial components｜Parts under the hood of a｜Power/Other Tools｜Metal substitution｜Valves/valve components｜Industrial applications｜Machine/mechanical compon｜Laptop case｜Application in the automo
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 23℃,24hr | % | 0.30到0.51 | |
| Flow,23℃,50%RH | % | 0.21到1.2 | |
| Flow:23℃ | mm/mm | 119.4E-3到0.254 | |
| 23℃,24hr | % | 0.12到0.30 | |
| Flow:23℃ | mm/mm | 48.3E-3到129.5E-3 |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flow | mm/mm/°C | 195.6E-5到25.4E-5 | |
| Vicat Softening Temperature | °C | 258到313 | |
| 8.0Mpa, Unannealed | °C | 165到230 | |
| 1.8MPa, Unannealed | °C | 247到292 | |
| 0.45MPa Annealed | °C | 296到320 | |
| 0.45MPa, Unannealed | °C | 275到308 | |
| RTI | °C | 119到150 | |
| Continuous Use Temperature | °C | 140到186 | |
| Flow | mm/mm/°C | 68.6E-5到127.0E-5 | |
| 1.8MPa, Unannealed | °C | 283到300 | |
| Flow | mm/mm/°C | 63.5E-5到177.8E-5 | |
| 0.45MPa, Unannealed | °C | 273到312 | |
| Evolution Calendar intelligent importer | °C | 118到150 | |
| RTIElec | °C | 140到150 | |
| Flow | mm/mm/°C | 38.1E-5到50.8E-5 | |
| 1.8MPa, Unannealed | °C | 249到304 | |
| Flow | mm/mm/°C | 185.4E-5到25.4E-5 |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Oxygen Index | % | 23到25 | |
| Glow Wire Flammability Index | °C | 743到960 | |
| Glow Wire Ignition Temperature | °C | 721到926 |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shearing Strength | 23℃ | MPa | 88.28到107.59 |
| Yield,23℃ | MPa | 102.76到362.76 | |
| Poisson Ratio | 23℃ | 0.41 | |
| Compressive Strength | 23℃ | MPa | 142.76到196.55 |
| Yield,23℃ | % | 1.4到2.5 | |
| Break,23℃ | % | 1.5到3.1 | |
| % | 1.0到2.5 | ||
| Tensile Modulus | 摩擦系数 | 0.15到0.52 | |
| Yield,23℃ | MPa | 68.97到250.34 | |
| Break,23℃ | MPa | 131.72到400.0 | |
| MPa | 162.76到199.31 | ||
| Yield,23℃ | % | 1.5到2.6 | |
| MPa | 12.62到270.34 | ||
| Break,23℃ | MPa | 108.28到262.76 |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Comparative Tracking Index | CTI | V | 548到600 |
| V | 593到600 |
| Hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell Hardness | 23℃ | 125 |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 4.178到19.964 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.