PA11 Rilsan® BMNO P40 TLD ARKEMA FRANCE
236
Unit Price:$12336 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability UV resistance Plasticized Photostability Good demolding performanc
- Application Areas:Electric wire Cable Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume-Flow Rate (MVR) | 235°C/2.16 kg | ISO 1133 | 11.0 | cm3/10min |
| Water absorption rate | Saturation, 23°C | ISO 62 | 1.6 | % |
| Saturation | ASTM D570 | 1.1 | % | |
| hardness | ASTM D785 | 78 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture tensile strength | ASTM D638 | 64.1 | Mpa | |
| elongation | Break | ASTM D638 | 430 | % |
| Bending modulus | ASTM D790 | 338 | Mpa | |
| Impact strength of cantilever beam gap | ASTM D256 | 320 | J/m | |
| Tensile modulus | ISO 527-2 | 405 | Mpa | |
| tensile strength | Yield | ISO 527-2 | 27.0 | Mpa |
| elongation | Yield | ISO 527-2 | 42 | % |
| Nominal tensile fracture strain | ISO 527-2 | > 50 | % | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | -- | |
| 23°C | ISO 179/1eU | -- |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 130 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 45.0 | °C | |
| vicat softening point | ISO 306/B50 | 140 | °C | |
| Melting temperature | ISO 11357-3 | 182 | °C | |
| Linear coefficient of thermal expansion - flow | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Melting temperature | DSC | 186 | °C | |
| Hot deformation temperature | 1.8MPa | QJ/CL.4.3.19 | 41.1 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | -- | ohms | |
| Volume resistivity | IEC 60093 | -- | ohms·cm | |
| Dielectric strength | IEC 60243-1 | -- | KV/mm | |
| Relative permittivity | 100 Hz | IEC 60250 | 10.0 | |
| 1 MHz | IEC 60250 | 4.00 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 0.18 | |
| 1 MHz | IEC 60250 | 0.096 | ||
| Leakage Trace Index | IEC 60112 | -- | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 1.6 mm | IEC 60695-11-10, -20 | HB | |
| 3.2 mm | IEC 60695-11-10, -20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 22 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.