PEI ULTEM™ 1000-1000 SABIC INNOVATIVE US
298
Unit Price:$22276 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 69.4MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Flame retardant enhance
- Application Areas:Automotive sector Electrical field Electronic field
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体质量流动速率 | 337°C/6.6 kg | ASTM D1238 | 9.0 | g/10 min |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| 吸水率 | 24 hr | ASTM D570 | 0.25 | % |
| 平衡, 23°C | ASTM D570 | 1.3 | % |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 洛氏硬度 | M 级 | ASTM D785 | 109 | |
| 拉伸模量 | ASTM D638 | 3580 | Mpa | |
| 拉伸强度 | 屈服 | ASTM D638 | 110 | Mpa |
| 伸长率 | 屈服 | ASTM D638 | 7.0 | % |
| 断裂 | ASTM D638 | 60 | % | |
| 弯曲模量 | 100 mm 跨距 | ASTM D790 | 3510 | Mpa |
| 弯曲强度 | 屈服, 100 mm 跨距 | ASTM D790 | 165 | Mpa |
| 泊松比 | ASTM E132 | 0.36 | ||
| 泰伯耐磨性 | 1000 Cycles, 1000 g, CS-17 转轮 | ASTM D1044 | 10.0 | mg |
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 1300 | J/m |
| 反向缺口冲击 | 3.20 mm | ASTM D256 | 1300 | J/m |
| 落锤冲击 | 23°C | ASTM D3029 | 36.0 | J |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 210 | °C |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 201 | °C | |
| 维卡软化点 | ASTM D15254 | 218 | °C | |
| 线性热膨胀系数 | 流动 : -20 到 150°C | ASTM E831 | 5.6E-5 | cm/cm/°C |
| 横向 : -20 到 150°C | ASTM E831 | 5.4E-5 | cm/cm/°C | |
| 导热系数 | ASTM C177 | 0.22 | W/m/K | |
| RTI Elec | UL 746 | 170 | °C | |
| RTI Imp | UL 746 | 170 | °C | |
| RTI | UL 746 | 170 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 体积电阻率 | ASTM D257 | 1.0E+17 | ohms·cm | |
| 介电强度 | 1.60 mm, in Air | ASTM D149 | 33 | KV/mm |
| 1.60 mm, in Oil | ASTM D149 | 28 | KV/mm | |
| 3.20 mm, in Oil | ASTM D149 | 20 | KV/mm | |
| 介电常数 | 100 Hz | ASTM D150 | 3.15 | |
| 1 kHz | ASTM D150 | 3.15 | ||
| 耗散因数 | 100 Hz | ASTM D150 | 1.5E-3 | |
| 1 kHz | ASTM D150 | 1.2E-3 | ||
| 2.45 GHz | ASTM D150 | 2.5E-3 | ||
| 耐电弧性 | ASTM D495 | PLC 5 | ||
| 相比耐漏电起痕指数(CTI) | UL 746 | PLC 4 | ||
| 高电弧燃烧指数(HAI) | UL 746 | PLC 3 | ||
| 高电压电弧起痕速率 (HVTR) | UL 746 | PLC 2 | ||
| 热丝引燃 (HWI) | UL 746 | PLC 1 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 150 | °C | ||
| 干燥时间 | 4.0 到 6.0 | hr | ||
| 建议的最大水分含量 | 0.020 | % | ||
| 建议注射量 | 40 到 60 | % | ||
| 料筒后部温度 | 330 到 400 | °C | ||
| 料筒中部温度 | 340 到 400 | °C | ||
| 料筒前部温度 | 345 到 400 | °C | ||
| 射嘴温度 | 345 到 400 | °C | ||
| 加工（熔体）温度 | 350 到 400 | °C | ||
| 模具温度 | 135 到 165 | °C | ||
| 背压 | 0.300 到 0.700 | Mpa | ||
| 螺杆转速 | 40 到 70 | rpm | ||
| 排气孔深度 | 0.025 到 0.076 | mm |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL 阻燃等级 | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | 5VA | ||
| 极限氧指数 | ASTM D2863 | 47 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.