PEEK VICTREX® 381G VICTREX UK
142
Unit Price:$102148 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO1183 | 1.30 | g/cm³ | |
| SpiralFlow3. | 内部方法 | 12.0 | CM | |
| Shrinkage rate | TD | ISO294-4 | 1.3 | % |
| MD | ISO294-4 | 1.0 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.45 | % |
| Water absorption rate - saturation | 100°C | ISO62 | 0.55 | % |
| MeltViscosity | 400°C | ISO11443 | 300 | Pa·s |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| bending strength | 3.5%Strain,23°C | ISO178 | 125 | Mpa |
| 23°C | ISO178 | 165 | Mpa | |
| 125°C | ISO178 | 85.0 | Mpa | |
| 175°C | ISO178 | 19.0 | Mpa | |
| 275°C | ISO178 | 12.5 | Mpa | |
| Compressive stress | 23°C | ISO604 | 125 | Mpa |
| 120°C | ISO604 | 70.0 | Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | NoBreak | |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 7.0 | kJ/m² |
| Tensile modulus | 23°C | ISO527-2 | 4000 | Mpa |
| tensile strength | Yield,23°C | ISO527-2 | 98.0 | Mpa |
| elongation | Break,23°C | ISO527-2 | 45 | % |
| Bending modulus | 23°C | ISO178 | 3800 | Mpa |
| Cantilever beam without notch impact strength | 23°C | ISO180 | NoBreak | |
| Shore hardness | Shore D,23°C | ISO868 | 85 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/Af | 152 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 160 | °C | |
| Glass transition temperature | --7 | ISO11357-2 | 143 | °C |
| --8 | ISO11357-2 | 150 | °C | |
| Melting temperature | ISO11357-3 | 343 | °C | |
| Linear coefficient of thermal expansion | MD：<143°C | ISO11359-2 | 4.5E-05 | cm/cm/°C |
| MD：>143°C | ISO11359-2 | 1.2E-04 | cm/cm/°C | |
| TD：<143°C | ISO11359-2 | 5.5E-05 | cm/cm/°C | |
| TD：>143°C | ISO11359-2 | 1.4E-04 | cm/cm/°C | |
| thermal conductivity | 23°C9 | ISO22007-4 | 0.29 | W/m/K |
| 23°C10 | ISO22007-4 | 0.32 | W/m/K | |
| RTIElec | UL746 | 260 | °C | |
| RTI Imp | UL746 | 180 | °C | |
| RTIStr | UL746 | 240 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
| 125°C | IEC60093 | 1E+15 | ohms·cm | |
| 275°C | IEC60093 | 1E+09 | ohms·cm | |
| Dielectric strength | 0.0500mm | IEC60243-1 | 190 | KV/mm |
| 2.00mm | IEC60243-1 | 23 | KV/mm | |
| Dielectric constant | 23°C,50Hz | IEC60250 | 3.20 | |
| 200°C,50Hz | IEC60250 | 4.50 | ||
| Dissipation factor | 23°C,1MHz | IEC60250 | 3E-03 | |
| Leakage Trace Index | IEC60112 | 150 | V |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | --11 | ISO4589-2 | 24 | % |
| --12 | ISO4589-2 | 35 | % | |
| toxicity | COcontent | NES713 | 0.0740 | |
| CO2content | NES713 | 0.150 | ||
| Totalgases | NES713 | 0.220 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Contact Us
Get App
Top