PEEK VICTREX® 450GL15 VICTREX UK
247
Unit Price:$89361 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 36MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced
- Application Areas:Non specific food Medical supplies Nursing supplies
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/Specific Gravity | ISO1183 | 1.38 | g/cm³ | |
| SpiralFlow | 内部方法 | 10.0 | CM | |
| Shrinkage rate | TD:180°C | ISO294-4 | 0.90 | % |
| MD:180°C | ISO294-4 | 0.50 | % | |
| Water absorption rate | 23°C,24hr,3.20mm | ISO62 | 0.060 | % |
| Equilibrium,23°C,3.20mm,50%RH | ISO62 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compressive stress | 120°C | ISO604 | 130 | Mpa |
| 200°C | ISO604 | 40.0 | Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.5 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1U | 60 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/A | 6.0 | kJ/m² |
| Cantilever beam without notch impact strength | 23°C | ISO180 | 55 | kJ/m² |
| Shore hardness | Shore D,23°C | ISO868 | 86 | |
| Tensile modulus | 23°C | ISO527-2 | 7500 | Mpa |
| tensile strength | Break,23°C | ISO527-2 | 140 | Mpa |
| Break,125°C | ISO527-2 | 80.0 | Mpa | |
| Break,175°C | ISO527-2 | 45.0 | Mpa | |
| Break,275°C | ISO527-2 | 25.0 | Mpa | |
| elongation | Break,23°C | ISO527-2 | 4.0 | % |
| Bending modulus | 23°C | ISO178 | 7000 | Mpa |
| bending strength | 23°C | ISO178 | 240 | Mpa |
| Compressive stress | 23°C | ISO604 | 200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD:>143°C | ISO11359-2 | 3E-05 | cm/cm/°C |
| TD:<143°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD:>143°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| specific heat | 23°C | DSC | 1700 | J/kg/°C |
| thermal conductivity | 23°C | ISO22007-4 | 0.30 | W/m/K |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/Af | 298 | °C |
| Glass transition temperature | ISO11357-2 | 143 | °C | |
| Melting temperature | ISO11357-3 | 343 | °C | |
| Linear coefficient of thermal expansion | MD:<143°C | ISO11359-2 | 2.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+16 | ohms·cm | |
| Dielectric strength | 2.00mm | IEC60243-1 | 24 | KV/mm |
| Dielectric constant | 23°C,1kHz | IEC60250 | 3.10 | |
| Dissipation factor | 23°C,1MHz | IEC60250 | 5E-03 | |
| Leakage Trace Index | IEC60112 | 150 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 400°C | ISO11443 | 450 | Pa·s |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.