PEEK KetaSpire® PEEK KT-820 SOLVAY USA
233
Unit Price:$79559 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 54MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Steam resistant Chemical resistance Dimensional stability Fatigue resistance High impact
- Application Areas:Laptop case Aircraft Applications Automotive Applications Dental applications Electronic and Electrical film Engine parts Medical devices Shell packing tubing
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD:3.18mm | ASTMD955 | 0.20到0.40 | % |
| TD:3.18mm | ASTMD955 | 1.4到1.6 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.10 | % |
| Melt mass flow rate | 400°C/2.16kg | ASTMD1238 | 0.70 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Poisson's ratio | 7.58 | 0.34 | ||
| Cantilever beam without notch impact strength | -- | ISO180 | 56 | kJ/m² |
| -- | ASTMD4812 | 960 | J/m | |
| Nominal tensile fracture strain | -- | ISO527-2/1A/5 | 2.7 | % |
| --6 | ASTMD638 | 2.7 | % | |
| Shore hardness | Shore D,1sec | ASTMD2240 | 91 | |
| compressive strength | ASTMD695 | 169 | Mpa | |
| shear strength | ASTMD732 | 93.1 | Mpa | |
| Tensile modulus | --5 | ASTMD638 | 10500 | Mpa |
| -- | ISO527-2/1A/1 | 11400 | Mpa | |
| tensile strength | Yield5 | ASTMD638 | 158 | Mpa |
| Yield | ISO527-2/1A/5 | 165 | Mpa | |
| -- | ASTMD638 | 158 | Mpa | |
| Rockwell hardness | M-Scale | ASTMD785 | 100 | |
| Bending modulus | -- | ASTMD790 | 10300 | Mpa |
| -- | ISO178 | 10700 | Mpa | |
| bending strength | -- | ASTMD790 | 271 | Mpa |
| -- | ISO178 | 246 | Mpa | |
| Yield | ASTMD790 | 261 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed | ASTMD648 | 315 | °C |
| specific heat | 50°C | DSC | 1300 | J/kg/°C |
| 200°C | DSC | 1730 | J/kg/°C | |
| thermal conductivity | ASTME1530 | 0.29 | W/m/K | |
| Peak melting temperature | ASTMD3418 | 340 | °C | |
| Glass transition temperature | ASTMD3418 | 150 | °C | |
| Linear coefficient of thermal expansion | MD：-50to50°C | ASTME831 | 1.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 60Hz | ASTMD150 | 1E-03 | |
| 1kHz | ASTMD150 | 1E-03 | ||
| 1MHz | ASTMD150 | 3E-03 | ||
| Dielectric strength | 3.00mm | ASTMD149 | 17 | KV/mm |
| Surface resistivity | ASTMD257 | >1.9E+17 | ohms | |
| Dielectric constant | 60Hz | ASTMD150 | 3.44 | |
| 1kHz | ASTMD150 | 3.44 | ||
| 1MHz | ASTMD150 | 3.41 | ||
| Volume resistivity | ASTMD257 | 1.9E+17 | ohms·cm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 400°C,1000sec^-1 | ASTMD3835 | 850 | Pa·s |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | V-0 | |
| 20.3mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.