PA46 Stanyl® TW200F6 DSM HOLAND

269

Unit Price:$6836 USD/MT

Packaging Specification:: 25 KG/PKG

Supply Quantity:: 108.6MT

Delivery Terms:: FOB

Port of Loading:: China Main Port

Accepted Payment Methods:: T/T

Shipping:: Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability
Application Areas:Electronic and electrical Casters
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
density		ISO 1183	1.41	g/cm³
Shrinkage rate	Across Flow	ISO 294-4	1.3	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.50	%
Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.6	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	--	ISO 527-2	10000	Mpa
	Tensile modulus	120°C	ISO 527-2	5500	Mpa
		Tensile modulus	160°C	ISO 527-2	5000	Mpa
			Tensile modulus	180°C	ISO 527-2	4400	Mpa
			Tensile modulus	Tensile modulus	200°C	ISO 527-2	4000	Mpa
tensile strength	Break	ISO 527-2	210	Mpa
	tensile strength	Break, 120°C	ISO 527-2	110	Mpa
		tensile strength	Break, 160°C	ISO 527-2	100	Mpa
			tensile strength	Break, 180°C	ISO 527-2	95.0	Mpa
			tensile strength	tensile strength	Break, 200°C	ISO 527-2	90.0	Mpa
elongation	Break	ISO 527-2	4.0	%
	elongation	Break, 120°C	ISO 527-2	7.5	%
		elongation	Break, 160°C	ISO 527-2	7.5	%
			elongation	Break, 180°C	ISO 527-2	7.5	%
			elongation	elongation	Break, 200°C	ISO 527-2	7.5	%
Bending modulus	--	ISO 178	9000	Mpa
	Bending modulus	120°C	ISO 178	4700	Mpa
	Bending modulus	Bending modulus	160°C	ISO 178	3900	Mpa
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	11	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	12	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	11	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	12	kJ/m²

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	290	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	290	°C
Melting temperature		ISO 11357-3	295	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.5E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	6.0E-5	cm/cm/°C
RTI Elec	0.9 mm	UL 746	140	°C
Thermal Index - 5000 hr		IEC 60216	177	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC 60093	1.0E+14	ohms·cm
Dielectric strength		IEC 60243-1	30	KV/mm
Relative permittivity	100 Hz	IEC 60250	4.30
Relative permittivity	Relative permittivity	1 MHz	IEC 60250	4.00
Leakage Trace Index		IEC 60112	300	V

flammability	Test Condition	Test Method	Test Result	Unit
Flammability level	0.75 mm	IEC 60695-11-10, -20	HB
Flammability level	Flammability level	1.5 mm	IEC 60695-11-10, -20	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.