PBT VALOX™ DR48-BK1066 SABIC INNOVATIVE SHANGHAI
258
Unit Price:$3797 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 60MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced
- Application Areas:Side track application Non specific food Lawn equipment Garden equipment Industrial applications Automotive External Parts Electrical field Electronic field Architectural application Outdoor applications Electrical appliances Engine hood parts Medical supplies Nursing supplies Plastic bag Automotive interior parts Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific volume | ASTM D792 | 0.650 | cm³/g | |
| Shrinkage rate | Flow : 1.50 to 3.20 mm | 内部方法 | 0.40 到 0.60 | % |
| Flow : 3.20 to 4.60 mm | 内部方法 | 0.60 到 0.90 | % | |
| Across Flow : 1.50 to 3.20 mm | 内部方法 | 0.50 到 0.80 | % | |
| Across Flow : 3.20 to 4.60 mm | 内部方法 | 0.80 到 1.1 | % | |
| Water absorption rate | 24 hr | ASTM D570 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 118 | |
| tensile strength | Break | ASTM D638 | 93.0 | Mpa |
| Bending modulus | 50.0 mm Span | ASTM D790 | 5200 | Mpa |
| bending strength | Break, 50.0 mm Span | ASTM D790 | 140 | Mpa |
| Non notched cantilever beam impact | 23°C | ASTM D4812 | 500 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 210 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 182 | °C | |
| Linear coefficient of thermal expansion - flow | -40 to 40°C | ASTM E831 | 2.0E-5 | cm/cm/°C |
| 60 to 138°C | ASTM E831 | 2.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 120 | °C | |
| RTI Imp | UL 746 | 120 | °C | |
| RTI | UL 746 | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 | ohms·cm | |
| Dielectric strength | 1.60 mm, in Oil | ASTM D149 | 25 | KV/mm |
| 3.20 mm, in Air | ASTM D149 | 19 | KV/mm | |
| Dielectric constant | 100 Hz | ASTM D150 | 3.60 | |
| 1 MHz | ASTM D150 | 3.40 | ||
| Dissipation factor | 100 Hz | ASTM D150 | 2.0E-3 | |
| 1 MHz | ASTM D150 | 0.016 | ||
| Arc resistance | ASTM D495 | PLC 6 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 120 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 80 | % | ||
| Temperature at the rear of the barrel | 240 到 255 | °C | ||
| Temperature in the middle of the barrel | 245 到 260 | °C | ||
| Temperature at the front of the material cylinder | 250 到 265 | °C | ||
| Spray nozzle temperature | 245 到 260 | °C | ||
| Processing (melt) temperature | 250 到 265 | °C | ||
| Mold temperature | 65 到 90 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 50 到 80 | rpm | ||
| Exhaust hole depth | 0.025 到 0.038 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.9 mm | UL 94 | V-0 | |
| 3.0 mm | UL 94 | 5VA | ||
| Extreme Oxygen Index | ASTM D2863 | 29 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.