Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Low warpage Glass fiber reinforced Filler: Glass fiber reinf 30% by weight ratio) 30% filler by weight Anti warping Good surface performance
- Application Areas:Electronic and electrical Automotive Applications Industrial applications Industrial applications Box/Shell/Cover/Set Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | -，Flow | ISO 294-4 | 0.30 | % |
| 密度 | ISO 1183 | g/cm | ||
| 收缩率 | -，Across Flow | ISO 294-4 | % | |
| 吸水率 | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.25 | % |
| 密度 | ISO1183 | 1.42 | g/cm³ | |
| 熔体质量流动速率 | ISO1133 | 13 | g/10min | |
| 熔体体积流动速率 | 250°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| 收缩率 | TD | ISO294-4 | 0.60 | % |
| MD | ISO294-4 | 0.30 | % | |
| 吸水率 | 饱和,23°C,2.00mm | ISO62 | 1.0 | % |
| MeltDensity | 1.27 | g/cm³ | ||
| 顶出温度 | 170 | °C | ||
| SpecificHeatCapacityofMelt | 1790 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.28 | W/m/K |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 拉伸模量 | ISO527-2 | 9800 | Mpa | |
| 拉伸强度 | 断裂 | ISO527-2 | 135 | Mpa |
| 伸长率 | 断裂 | ISO527-2 | 2.3 | % |
| 弯曲模量 | ISO178 | 8400 | Mpa | |
| 简支梁缺口冲击强度 | -40°C | ISO179/1eA | 9.0 | kJ/m² |
| -30°C | ISO179/1eA | 9.0 | kJ/m² | |
| 23°C | ISO179/1eA | 9.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | -40°C | ISO179/1eU | 50 | kJ/m² |
| 23°C | ISO179/1eU | 55 | kJ/m² | |
| 悬壁梁缺口冲击强度 | -40°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 7.0 | kJ/m² | |
| 悬臂梁无缺口冲击强度 | -40°C | ISO180/1U | 45 | kJ/m² |
| 23°C | ISO180/1U | 45 | kJ/m² | |
| 缺口冲击强度 | -，-40 °C, Type 1, Notch A | ISO 180 | KJ/m | |
| -，23 °C, Type 1, Notch A | ISO 180 | KJ/m | ||
| 断裂点拉伸应力 | 23℃ | ISO 527-1, -2 | Mpa | |
| 断裂点拉伸应变 | ISO 527-1, -2 | 2.3 | % | |
| 拉伸模量 | 23℃ | ISO 527-1, -2 | 9800 | Mpa |
| 弯曲模量 | 23℃ | ISO 178 | Mpa | |
| Charpy 非缺口冲击强度 | 23 ℃, Type 1, Edgewise | ISO 179 | 55 | KJ/m |
| 简支梁缺口冲击强度 | 23 ℃, Type 1, Edgewise, Notch A | ISO 179 | KJ/m | |
| 非缺口冲击强度 | -，-40 ℃, Type 1 | ISO 180 | 55 | KJ/m |
| -，23 ℃, Type 1 | ISO 180 | KJ/m |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔融温度 | ISO 3146 | ℃ | ||
| 热变形温度 | 1.80 Mpa，未退火 | ISO 75A-1, -2 | 185 | ℃ |
| 阻燃等级 | -，0.750 mm | UL 94 | HB | |
| -，1.50 mm | UL 94 | HB | ||
| -，3.00 mm | UL 94 | HB | ||
| 热变形温度 | 1.8MPa,未退火 | ISO75-2/A | 185 | °C |
| 熔融温度 | ISO11357-3 | 225 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 表面电阻率 | IEC60093 | >1.0E+15 | ohms | |
| 漏电起痕指数 | IEC60112 | 550 | V |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 燃烧速率 | 1.00mm | ISO3795 | 28 | mm/min |
| UL阻燃等级 | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS可燃性 | FMVSS302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.