PPO NORYL™ N1250 BK1066 SABIC INNOVATIVE SHANGHAI
231
Unit Price:$3929 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 28MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan High mobility Glass fiber reinforced
- Application Areas:Automotive interior parts Electrical applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/5.0 kg | ASTM D1238 | 28 | g/10 min |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM D638 | 2680 | Mpa | |
| tensile strength | Yield | ASTM D638 | 75.0 | Mpa |
| Break | ASTM D638 | 64.0 | Mpa | |
| Elongation rate | Yield | ASTM D638 | 4.6 | % |
| Break | ASTM D638 | 25 | % | |
| Bending modulus | 50.0 mm Span | ASTM D790 | 2680 | Mpa |
| bending strength | Yield, 50.0 mm Span | ASTM D790 | 113 | Mpa |
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 40.0 | J |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 131 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 133 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 116 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 122 | °C | |
| vicat softening point | ASTM D15255 | 137 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.1E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 6.8E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 110 | °C | |
| RTI Imp | UL 746 | 105 | °C | |
| RTI | UL 746 | 115 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc resistance | ASTM D495 | PLC 6 | ||
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) | UL 746 | PLC 0 | ||
| High Voltage Arc Resistance Index (HVAR) (PLC) | UL 746 | PLC 4 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 105 到 110 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 245 到 295 | °C | ||
| Temperature in the middle of the barrel | 255 到 300 | °C | ||
| Temperature at the front of the material cylinder | 265 到 305 | °C | ||
| Spray nozzle temperature | 275 到 305 | °C | ||
| Processing (melt) temperature | 275 到 305 | °C | ||
| Mold temperature | 70 到 100 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.76 mm | UL 94 | V-0 | ||
| 2.5 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.