PPO NORYL™ PX9406P-7001 SABIC INNOVATIVE JAPAN
237
Unit Price:$4043 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Electronic communication Electronic communication building materials Profile
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 250°C/10.0 kg | ASTM D1238 | 3.9 | g/10 min |
| Melt Volume-Flow Rate (MVR) | 280°C/10.0 kg | ISO 1133 | 27.0 | cm3/10min |
| 280°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 300°C/5.0 kg | ISO 1133 | 23.0 | cm3/10min | |
| Shrinkage rate - flow | 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Water absorption rate | 24 hr | ASTM D570 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Yield | 内部方法 | 63.0 | Mpa |
| Yield | ISO 527-2/50 | 73.0 | Mpa | |
| elongation | Break | 内部方法 | 85 | % |
| Break | ISO 527-2/50 | 4.5 | % | |
| Bending modulus | -- | ASTM D790 | 2350 | Mpa |
| -- 2 | ISO 178 | 2600 | Mpa | |
| bending strength | -- | ASTM D790 | 99.0 | Mpa |
| -- 2, 3 | ISO 178 | 108 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 9.0 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 136 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 125 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 5 | ISO 75-2/Af | 117 | °C | |
| vicat softening point | -- | ISO 306/A120 | 151 | °C |
| -- | ISO 306/B120 | 142 | °C | |
| Ball Pressure Test | 125°C | IEC 60695-10-2 | 通过 | |
| Linear coefficient of thermal expansion | Flow : -30 to 30°C | TMA | 7.0E-5 | cm/cm/°C |
| Flow : -40 to 40°C | ISO 11359-2 | 6.6E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTM D257 | 1.0E+16 | ohms | |
| Dielectric constant | 60 Hz | ASTM D150 | 2.80 | |
| 50 kHz | ASTM D150 | 2.80 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 280°C, 1500 sec^-1 | ISO 11443 | 278 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 105 到 110 | °C | ||
| drying time | 3.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 30 到 70 | % | ||
| Temperature at the rear of the barrel | 245 到 295 | °C | ||
| Temperature in the middle of the barrel | 255 到 300 | °C | ||
| Temperature at the front of the material cylinder | 265 到 305 | °C | ||
| Spray nozzle temperature | 275 到 305 | °C | ||
| Processing (melt) temperature | 275 到 305 | °C | ||
| Mold temperature | 70 到 100 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.038 到 0.051 | mm |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.40 mm | UL 94 | V-2 | |
| 0.75 mm | UL 94 | V-0 | ||
| 2.5 mm | UL 94 | 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.