برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.12 g/cm³ |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 15 g/10min |
| Shrinkage rate | | 内部方法 | 0.55 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| Hot filament ignition temperature | | IEC 60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ASTM D2863 | 21 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation | Break | ASTM D638 | 50 % |
| Flexural modulus | | ASTM D790 | 2250 MPa |
| tensile strength | Yield | ASTM D638 | 50.0 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of cantilever beam gap | -30°C | ASTM D256 | 200 J/m |
| Impact strength of cantilever beam gap | 0°C | ASTM D256 | 300 J/m |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 400 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 90.0 °C |
| vicat | | ASTM D15252 | 110 °C |
| ball-indentation hardness | 75°C | IEC 335 | 通过 |
نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.
مقایسه