| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 1.3 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.9 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.6mm | UL 94 | V-2 |
| UL flame retardant rating | 3.2mm | UL 94 | V-2 |
| Burning wire flammability index | 0.8mm | IEC 60695-2-12 | 650 °C |
| GWIT | 1.6mm | IEC 60695-2-13 | 650 °C |
| Limiting Oxygen Index | | ISO 4589-2 | 26 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 3200 Mpa |
| tensile strength | 屈服,23°C | ASTM D638 | 85.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2/1A | 85.0 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/1A | 55.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.5 % |
| elongation | 断裂,23°C | ASTM D638 | 30 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | >30 % |
| Flexural modulus | 23°C | ASTM D790 | 3000 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2800 Mpa |
| bending strength | 23°C | ASTM D790 | 125 Mpa |
| bending strength | 23°C | ISO 178 | 120 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | IEC 60093 | 1E+15 ohms |
| Volume resistivity | | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 25 KV/mm |
| relative permittivity | | IEC 60250 | 2.90 |
| Dissipation Factor | | IEC 60250 | 0.030 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案B | IEC 60112 | PLC 1 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648 | 220 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/Bf | 200 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/Af | 75.0 °C |
| melting temperature | | ISO 11357-3 | 263 °C |