optical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Refractive index		ISO 489	1.586
turbidity	3000μm	ISO 14782	<0.80	%
transmissivity	1000μm	ISO 13468-2	89.0	%
	transmissivity	2000μm	ISO 13468-2	89.0	%
		transmissivity	3000μm	ISO 13468-2	88.0	%
		transmissivity	transmissivity	4000μm	ISO 13468-2	87.0	%
impact performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Multi axis Instrumented Peak Impact Force	23°C	ISO 6603-2	5400	N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	-30°C	ISO 6603-2	6300	N
Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	60.0	J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	-30°C	ISO 6603-2	65.0	J
Impact strength of cantilever beam gap	23°C,Partial Break	ISO 7391	70	kJ/m²
Charpy Notched Impact Strength	-30°C,Complete Break	ISO 7391	16	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C,Partial Break	ISO 7391	70	kJ/m²
Impact strength of simply supported beam without notch	-60°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Impact strength of cantilever beam gap	-30°C,Complete Break	ISO 7391	15	kJ/m²
flammability	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Burning wire flammability index	3.0mm	IEC 60695-2-12	930	°C
Hot filament ignition temperature	0.75mm	IEC 60695-2-13	875	°C
	Hot filament ignition temperature	1.5mm	IEC 60695-2-13	875	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875	°C
Burning wire flammability index	1.5mm	IEC 60695-2-12	850	°C
Extreme Oxygen Index		ISO 4589-2	27	%
FlashIgnitionTemperature		ASTM D1929	480	°C
SelfIgnition		ASTM D1929	550	°C
mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Tensile modulus	23°C	ISO 527-2/1	2400	Mpa
tensile strength	Yield,23°C	ISO 527-2/50	66.0	Mpa
tensile strength	tensile strength	Break,23°C	ISO 527-2/50	70.0	Mpa
Tensile strain	Yield,23°C	ISO 527-2/50	6.1	%
Tensile strain	Tensile strain	Break,23°C	ISO 527-2/50	130	%
Nominal tensile fracture strain	23°C	ISO 527-2/50	>50	%
Tensile creep modulus	1hr	ISO 899-1	2200	Mpa
Tensile creep modulus	Tensile creep modulus	1000hr	ISO 899-1	1900	Mpa
Bending modulus	23°C	ISO 178	2400	Mpa
bending strength	3.5%Strain,23°C	ISO 178	73.0	Mpa
bending strength	bending strength	23°C	ISO 178	97.0	Mpa
Bending strain	23°C	ISO 178	7.1	%
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
thermal conductivity	23°C	ISO 8302	0.20	W/m/K
Linear coefficient of thermal expansion	TD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23to55°C	ISO 11359-2	6.5E-05	cm/cm/°C
Ball Pressure Test	136°C	IEC 60695-10-2	Pass
Vicat softening temperature	--	ISO 306/B120	145	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	144	°C
Glass transition temperature		ISO 11357-2	145	°C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	124	°C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	137	°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Apparent density		ISO 60	0.66	g/cm³
melt mass-flow rate	300°C/1.2kg	ISO 1133	13	g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	12.0	cm3/10min
Shrinkage rate	TD	ISO 2577	0.60-0.80	%
	Shrinkage rate	MD	ISO 2577	0.60-0.80	%
		Shrinkage rate	TD:2.00mm3	ISO 294-4	0.75	%
		Shrinkage rate	Shrinkage rate	MD:2.00mm3	ISO 294-4	0.70	%
Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.12	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Compared to the anti leakage trace index	SolutionA	IEC 60112	PLC 2
Dissipation factor	23°C,1MHz	IEC 60250	9.5E-03
Dissipation factor	Dissipation factor	23°C,100Hz	IEC 60250	5E-04
Relative permittivity	23°C,1MHz	IEC 60250	3.00
Relative permittivity	Relative permittivity	23°C,100Hz	IEC 60250	3.10
Dielectric strength	23°C,1.00mm	IEC 60243-1	34	KV/mm
Volume resistivity	23°C	IEC 60093	1E+16	ohms·cm
Surface resistivity		IEC 60093	1E+16	ohms
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Ball Pressure Test		ISO 2039-1	115	Mpa