برگه داده فنی
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D4894 | 2.16 g/cm³ |
| Apparent density | | ASTM D4894 | 0.46 g/cm³ |
| Shrinkage rate | MD | 内部方法 | 4.4 % |
| Supplementary Information | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Breakdown voltage strength | 100.0µm | | 10 kV/mm |
| MITFlexuralLife | | ASTM D2178 | 5E+06 |
| StretchingVoidIndex | | ASTM D4895 | 300 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,1.50mm | ASTM D4894 | >43.0 MPa |
| elongation | 断裂,1.50mm | ASTM D4894 | >400 % |
| compressive strength | 0%应变2 | ASTM D695 | 7.80 MPa |
| compressive strength | 1%应变3 | ASTM D695 | 5.00 MPa |
| compressive strength | 25%应变3 | ASTM D695 | 28.1 MPa |
| Heat distortion temperature | 25°C,14MPa，HDT | ASTM D621 | 17.2 % |
| Heat distortion temperature | 100°C,14MPa，HDT | ASTM D621 | 33.3 % |
| Heat distortion temperature | 200°C,6.9MPa，HDT | ASTM D621 | 27.0 % |
| elastomer | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| compression set | 25°C4 | ASTM D621 | 8.6 % |
| compression set | 100°C4 | ASTM D621 | 20 % |
| compression set | 200°C5 | ASTM D621 | 16 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Surface Resistivity | | ASTM D257 | >1.0E+15 ohms |
| Volume resistivity | | ASTM D257 | >1.0E+18 ohms·cm |
| Dissipation Factor | 1kHz | ASTM D150 | <1.0E-4 |
| dielectric strength | | | 100 kV/mm |
| dielectric constant | 1kHz | ASTM D150 | <2.10 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Continuous use temperature | | | 260 °C |
| melting temperature | | DSC | 327 °C |