physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
density | | ASTM D792 | 0.9175 g/cm³ |
melt mass-flow rate | ℃/Kg | ASTM D1238 | 1.0 g/10min |
melt mass-flow rate | 厚度 | | 50.8 microns |
melt mass-flow rate | Antiblock水平 | | 2500 ppm |
melt mass-flow rate | 滑水平 | | 1000 ppm |
optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
gloss | | ASTM2457 | 64 |
Haze ratio | | ASTM D1003 | 13 % |
Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
impact force | | | 18 ft-lbf/in3 |
elongation | Break | ASTM D882 | 572 % |
elongation | Break | ASTM D882 | 612 % |
Elmendorf tear strength | | ASTM D192 | 780 g |
Elmendorf tear strength | | ASTM D192 | 975 g |
Dart impact | | ASTM D1709 | >=850 g |
tensile strength | | ASTM D882 | 8.267 MPa |
tensile strength | | ASTM D882 | 8.811 MPa |
Secant modulus | | ASTM D882 | 180.9 MPa |
Secant modulus | | ASTM D882 | 204.4 MPa |
tensile strength | | ASTM D882 | 38.04 MPa |
tensile strength | | ASTM D882 | 36.54 MPa |
Other performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
impact force | | ASTM D882 | 168 ft-lbf/in3 |
Puncture Resistance | | | 5.76 J |
Elmendorf tear strength | | ASTM D1922 | 15.4 g/micron |
Elmendorf tear strength | | ASTM D1922 | 19.19 g/micron |
Starting temperature of heat sealing | | | 95.0 °C |
Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
---|
vicat | | ASTM1525 | 100 °C |
vicat | Melting Temperature | 陶氏化学方法(DSC | 123 °C |