mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Friction coefficient	静态	ASTM D3702	0.35
tensile strength	23°C	ASTM D638	80	Mpa
Elongation at Break	23°C	ASTM D638	>15	%
Tensile modulus	23°C	ASTM D638	4200	Mpa
Tensile modulus	Tensile modulus	泊松比		7.58	0.38
bending strength	23°C	ASTM D790	130	Mpa
Bending modulus	23°C	ASTM D790	3800	Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	40	J/m
Friction coefficient	动态	ASTM D3702	0.40
thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Hot deformation temperature	0.45MPaUnannealed	ASTM D648	200	°C
Hot deformation temperature	Hot deformation temperature	1.80MPaUnannealed	ASTM D648	110	°C
Linear coefficient of thermal expansion	MD	ASTM D696	4E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTM D696	4E-05	cm/cm/°C
Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Shrinkage rate	MD	ASTM D995	1.30	%
Shrinkage rate	Shrinkage rate	TD	ASTM D995	1.50	%
Water absorption rate	(23°C,24hr)	ASTM D570	0.02	%
Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Volume resistivity		ASTM D257	1E+16	Ω.cm
Dielectric strength	1.60mm	ASTM D149	23	KV/mm
Dielectric constant	23°C	ASTM D150	3.3	1MHz
Dissipation factor	23°C	ASTM D150	2E-03	1MHz
	Dissipation factor	耐电弧性	ASTM D495	125	S
	Dissipation factor	Dissipation factor	相对漏电起痕指数	ASTM D3638	135	V
hardness	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
Rockwell hardness		ASTM D785	100	M（Scale）
Rockwell hardness	Rockwell hardness		ASTM D785	121	R
flame retardant performance	شرایط آزمون	روش آزمون	نتیجه آزمون	واحد آزمایش
UL flame retardant rating		UL -94	V-0	0.75mm