| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792 | 1.21 g/cm³ |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 9.0to16 g/10min |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 0.50to0.70 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | M计秤 | ASTM D785 | 70 |
| Rockwell hardness | R-Scale | ASTM D785 | 118 |
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| transmissivity | 2540µm | ASTM D1003 | 85.0 % |
| Haze ratio | 2540µm | ASTM D1003 | 1.0 % |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-2 |
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| tensile strength | 屈服,3.17mm | ASTM D638 | 62.1 MPa |
| tensile strength | Break,3.18mm | ASTM D638 | 55.2 MPa |
| elongation | 屈服,3.18mm | ASTM D638 | 7.0 % |
| elongation | 断裂,3.18mm | ASTM D638 | 90 % |
| Flexural modulus | 3.17mm | ASTM D790 | 2210 MPa |
| bending strength | Break,3.18mm | ASTM D790 | 89.6 MPa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Dart impact | 3.18mm | ASTM D3029 | 36.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 640 J/m |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1E+15 ohms·cm |
| dielectric strength | 1.50mm | ASTM D149 | 25 kV/mm |
| arc resistance | 1.50mm | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | 1.50mm | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 1.5mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 2 |
| Hot wire ignition (HWI) | 3.0mm | UL 746 | PLC 1 |
| High Voltage Arc Traceability Rate (HVTR) | 1.50mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 1.5mm | UL 746 | PLC 2 |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| RTI Str | 1.5mm | UL 746 | 125 °C |
| RTI Str | 3.0mm | UL 746 | 125 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 135 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 129 °C |
| vicat | | ASTM D15252 | 146 °C |
| RTI Elec | 1.5mm | UL 746 | 125 °C |
| RTI Elec | 3.0mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 110 °C |