Cellulose, Regenerated NatureFlex™ NVS 90
0
مقایسهبرگه داده فنی
| optical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| gloss | 45°,23.4µm | ASTM D2457 | 110 |
| Haze ratio | 23.4µm | ASTM D1003 | 4.0 % |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| coefficient of friction | Itself - Dynamic | ASTM D1894 | 0.25 |
| Itself - Static | ASTM D1894 | 0.25 |
| film | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|---|---|---|
| Secant modulus | 1%正割,MD:23µm | ASTM D882 | >3000 MPa |
| 1%正割,TD:23µm | ASTM D882 | >1520 MPa | |
| tensile strength | MD:屈服,23µm | ASTM D882 | 124 MPa |
| oxygen permeability | 24°C,23µm,0.0%RH，湿 | ASTMF1927 | 3.10 cm³/m²/24hr |
| Water Vapor Transmission Rate | ASTME96 | 370 g/m²/24hr | |
| film thickness | 内部方法 | 23.4 µm | |
| usage | 23.4µm | 内部方法 | 29.9 m²/kg |
| tensile strength | TD:屈服,23µm | ASTM D882 | 68.9 MPa |
| elongation | MD:断裂,23µm | ASTM D882 | 22 % |
| TD:断裂,23µm | ASTM D882 | 70 % | |
| Sealing emphasis | 内部方法 | 0.12 N/mm | |
| Initial sealing temperature | 23µm | 内部方法 | 90.6to199 °C |